Lomna žilavost visokotrdnostnih zvarnih spojev

diplomsko delo visokošolskega strokovnega študijskega programa 1. stopnje

Boštjan Vizlar (Author), Zdravko Praunseis (Mentor), Jurij Avsec (Co-mentor)

Abstract

Glede na varivost poboljšanih visokotrdnostnih malolegiranih konstrukcijskih (VTML) jekel ter predvsem s stališča ekonomičnosti je izvedba zvara z manjšo napetostjo tečenja oziroma z "mehkimi" korenskimi sloji (uporaba elektrod z manjšo napetostjo tečenja) zaželena, če lahko dosežemo veliko žilavost zvara, ki ne bo ogrožala varnega obratovanja zvarjenih konstrukcij. V diplomskem delu sem preučeval lomne lastnosti večvarkovnega z manjšo trdnostjo X zvarnega spoja z mehkim korenskim slojem in brez njega. Zvarni spoj je varjen na VTML-jeklu (debeline 30 mm) Niomol 490 in v zaščiteni atmosferi plina (80 % Ar+ 20 % CO2). V primeru X-zvarnega spoja z mehkim korenskim slojem je opazen vpliv mehkega korenskega sloja z najmanjšo trdnostjo na lomno žilavost CTOD celotnega zvarnega spoja, ki se je odražal na začetku krhkega loma v področju zvara z najmanjšo trdnostjo. Namen raziskave je ugotoviti, ali je izbrana tehnologija varjenja za trdnostno manjši zvarni spoj z mehkim korenskim slojem priporočljiva oziroma uporabna za izboljšanje varivosti VTML-jekla Niomol 490 glede na doseženo lomno žilavost zvara oziroma mehkega korenskega sloja.

Keywords

trdnostna neenakost;manjša trdnost zvara;mehki korenski sloj;lomna žilavost;CTOD-preizkus;lokalno krhka področja;

Data

Language:	Slovenian
Year of publishing:	2012
Source:	Krško
Typology:	2.11 - Undergraduate Thesis
Organization:	UM FE - Faculty of Energetics
Publisher:	[B. Vizlar]
UDC:	621.791.053:620.179.2(043.2)
COBISS:	1024105820
Views:	2194
Downloads:	201
Average score:	0 (0 votes)
Metadata:

Other data

Secondary language:	English
Secondary title:	Fracture toughness of HSLA steel welds
Secondary abstract:	In welds of quenched and tempered (Q + T) high strength low alloyed steels (HSLA) weld strength under matching can be used to satisfy the toughness requirements for the weld deposit. Cost of reduced pre-heating of these steels can be saved if one can prove that use of soft electrodes for root passes do not endanger the overall quality of the joint. The present work deals with the determination of Charpy impact toughness and CTOD fracture toughness of under matched X-grooved multy pass weld joints with soft and without soft root layer mode on HSLA steel (300 mm thick) grade HT 80. CTOD values were clearly influenced by the softer material in the root layer. The metallographical post-test sectioning has revealed the initiation points (LBZs) mainly at the lowest weld metal strength. The aim of this experimental work is to establish the fracture behavior of HLSA multy-pass mismatched welds and to determine the effect of local strength mismatch on fracture toughness and finally to prove that the welding procedure for the weld joint with a soft root layer improves the weld ability of commercial HLSA steel.
Secondary keywords:	strength mismatching;under matched welds;soft root layer;fracture toughness;CTOD test;local brittle zones;
URN:	URN:SI:UM:
Type (COBISS):	Bachelor thesis/paper
Thesis comment:	Dipl. delo, Univ. Maribor, Fakulteta za energetiko
Pages:	IX, 57 str.
Keywords (UDC):	applied sciences;medicine;technology;uporabne znanosti;medicina;tehnika;engineering;technology in general;inženirstvo;tehnologija na splošno;mechanical engineering in general;nuclear technology;electrical engineering;machinery;strojništvo;mechanical technology in general: processes;tools;machines;equipment;obdelava z deformacijo;obdelava brez odrezovanja;toplotna obdelava;applied sciences;medicine;technology;uporabne znanosti;medicina;tehnika;engineering;technology in general;inženirstvo;tehnologija na splošno;materials testing;commercial materials;power stations;economics of energy;preiskava materiala;blagoznanstvo;energetske centrale;energetika;