Sebastjan Žagar (Author), Hitoshi Soyama (Author), Janez Grum (Author), Roman Šturm (Author)

Abstract

The present paper aims to investigate topographical behavior of precipitation hardened magnesium alloy AZ80A subjected to cavitation peening. The introduction of surface residual compressive stress is the main feature of this new method, which is different from the traditional mechanical processing method and is also the key factor leading to the good service performance of the metal material surface. The tested material was heat treatable magnesium alloy AZ80A. Magnesium alloys have the lowest density among the common non-ferrous alloys and so are very important in reducing the weight and are used in many fields, including aviation, aerospace, electronics and automobile industries. After heat treatment of the magnesium alloy, cavitation peening was performed, which in all cases raises the surface hardness of the specimens. Cavitation peening also has a beneficial effect on compressive residual stresses, as they increase in all cases. It should be noted that in all specimens throughout the entire measurement depth the residual stresses stayed in compressive nature. They are especially expressed in the case of artificial aging, where we also achieve the maximum stress on the specimen surface in the amount of −220 MPa. The most negative thing about such a process is the surface roughness after cavitation hardening as it is greatly increased in all cases.

Keywords

magnesium alloy AZ80A;cavitation peening;artificial ageing;residual stresses;microhardness;surface roughness;microstructure;

Data

Language: English
Year of publishing:
Typology: 1.01 - Original Scientific Article
Organization: UL FS - Faculty of Mechanical Engineering
UDC: 669:620.1
COBISS: 97813507 Link will open in a new window
ISSN: 2238-7854
Views: 293
Downloads: 98
Average score: 0 (0 votes)
Metadata: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Other data

Secondary language: Slovenian
Secondary keywords: magnezijeva zlitina AZ80;kavitacijsko utrjevanje;umetno staranje;zaostale napetosti;mikrotrdota;površinska hrapavost;mikrostruktura;
Type (COBISS): Article
Pages: str. 2098-2107
Issue: ǂVol. ǂ17
Chronology: Mar./Apr. 2022
DOI: 10.1016/j.jmrt.2022.01.156
ID: 14554088
Recommended works:
, no subtitle data available
, no subtitle data available
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
, zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo