doctoral disertation
Fidan Smaili (Author), Tomaž Vuherer (Mentor)

Abstract

This research presents two possibilities to prepare and test the Fine Grain of a Heat Affected Zone, which, practically, could be considered as the weakest part of welded joints in the presence of any microdefect. It is a narrow zone located between the fusion zone and the unaffected base material; therefore, only a few methods are suitable to test its mechanical properties. The 18CrNiMo7-6 steel was used as the base material. As this steel is usually used for the production of dynamically loaded components, testing of its fatigue behaviour and fracture toughness was crucial, but also measurement of its hardness and impact toughness. To investigate the mechanical properties of a Fine-Grain Heat-Affected Zone (FG HAZ), two different methods for simulation of as-welded microstructures were used in this research: A weld thermal cycle simulator (WTCS) and austenitising in a laboratory furnace +

Keywords

weld joint;Fine Grain Heat Affected Zone;mechanical properties;fatigue crack growth;

Data

Language: English
Year of publishing:
Typology: 2.08 - Doctoral Dissertation
Organization: UM FS - Faculty of Mechanical Engineering
Publisher: [F. Smaili]
UDC: 620.178.3:621.791.053(043.3)
COBISS: 169316867 Link will open in a new window
Views: 31
Downloads: 2
Average score: 0 (0 votes)
Metadata: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Other data

Secondary language: Slovenian
Secondary title: Vpliv mikronapak na lastnosti pri utrujanju drobno zrnato toplotno vplivanega področja na nikelj-molibdenovem jeklu
Secondary abstract: Ta raziskava predstavlja dve možnosti za pripravo in preskušanje drobnozrnate toplotno prizadete cone, ki bi jo praktično lahko šteli za najšibkejši del varjenih spojev ob prisotnosti kakršne koli mikrodefekcije. Gre za ozko cono, ki se nahaja med cono taljenja in neoviranim osnovnim materialom, zato je za preskušanje njenih mehanskih lastnosti primernih le nekaj metod. Kot osnovni material je bilo uporabljeno jeklo 18CrNiMo7-6. Ker se to jeklo običajno uporablja za izdelavo dinamično obremenjenih sestavnih delov, je bilo ključno preskušanje njegovega obnašanja pri utrujanju in lomne trdnosti, pa tudi merjenje njegove trdote in udarne žilavosti. Da bi raziskali mehanske lastnosti toplotno prizadete cone s finimi zrni (FG HAZ), sta bili v tej raziskavi uporabljeni dve različni metodi za simulacijo mikrostruktur med varjenjem: Simulator toplotnega cikla varjenja (WTCS) in avstenitizacija v laboratorijski peči + kaljenje z vodo (AF+WQ). Mikrostruktura simuliranih vzorcev je bila zelo podobna resnični zvarjeni FG HAZ. Vzorci WTCS so imeli trdoto 419 HV, KV = 101,5 J, ΔKthR = 3,40 MPam0,5, C = 1,64 × 10-11, m = 2,4465. Pri vzorcih AF+WQ je bila trdota 425 HV, KV = 73,1 J, ΔKthR = 4,33 MPam0,5, C = 1,73×10-11, m = 2,5114. Trdota pravega zvara FG HAZ je bila 405 HV. Primerjava rezultatov za obe vrsti simuliranih vzorcev, med seboj in z rezultati za pravo HAZ zvara, je potrdila, da sta obe vrsti simuliranih vzorcev primerni za mehanske preskuse posameznih podobmočij Območje, na katerega vpliva toplota.
Secondary keywords: zvarni spoj;drobnozrnato toplotno vplivano področje;mehanske lastnosti;širjenje utrujenostne razpoke;doktorske disertacije;Univerzitetna in visokošolska dela;
Type (COBISS): Doctoral dissertation
Thesis comment: Univ. v Mariboru, Fak. za strojništvo
Pages: XXV, 161 f.
ID: 18440302