Matej Drobne (Avtor), Tomaž Vuherer (Avtor), Ivan Samardžić (Avtor), Srečko Glodež (Avtor)

Povzetek

Fatigue crack growth and fracture mechanics analysis of a working roll surface layer material is presented in this paper. The research is done on a hot strip mill working roll where High Chromium Steel is used for roll’s shell material. To obtain corresponding parameters, a rectangular single edge notched bend specimens – SENB, according to standard BS 7448, were used. The fatigue crack growth analysis was done on a resonant testing machine with use of special crack gauges, while for fracture mechanics parameters the electro–mechanical testing machine was used.

Ključne besede

mehanika loma;rast razpoke;rast utrujenostne razpoke;utrujenost materiala;visoko legirano kromovo jeklo;preiskava materiala;fracture mechanics;fatigue crack growth;metal forming;rolling process;high chromium steel;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UM FS - Fakulteta za strojništvo
UDK: 539.42:621.77
COBISS: 17828886 Povezava se bo odprla v novem oknu
ISSN: 0543-5846
Št. ogledov: 693
Št. prenosov: 101
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarne ključne besede: mehanika loma;rast razpoke;rast utrujenostne razpoke;utrujenost materiala;visoko legirano kromovo jeklo;preiskava materiala;
URN: URN:SI:UM:
Vrsta dela (COBISS): Znanstveno delo
Strani: str. 481-484
Letnik: ǂVol. ǂ53
Zvezek: ǂno. ǂ4
Čas izdaje: 2014
ID: 10846217