Tungsten carbide thin films for electrochemical water splitting studies

Saim Emin (Avtor), Matjaž Valant (Avtor)

Povzetek

We used wet-chemistry techniques to prepare colloidal tungsten (W) nanoparticles (NPs). The synthesis of W NPs was conducted using the so called hot-matrix method in 1-octadecene [1]. The sizes of obtained W NPs are in the order of 2 - 5 nm. These W NPs are coated with hydrophobic molecules which allow their dispersion in organic solvents like choloroform (CHCl3). It was found that the colloidal stability of the dispersions is exceptionally high exceeding several years. The stability of W NPs which prevents coagulation allows the preparation of thin films with uniform thicknesses by spin-coating, inkjet-printing and spray coating. We have prepared tungsten carbide (W2C, WC) thin films. The preparation of W2C and WC was achieved by spin-coating of pre-synthesized W NPs on graphite substrate and following heat treatment under Ar atmosphere at 1000 and 1450°C. The obtained W2C and WC films were used both in electrochemical water splitting studies. We also made a composite W2C-Pt films where we used only 5 at.% of Pt. The W2C-Pt composite has shown similar performance as pure Pt-C for hydrogen (H2) evolution. In conclusion, we have developed a procedure for the synthesis of W NPs which can be applied for the preparation of tungsten carbides films and their use for electrochemical water splitting.

Ključne besede

water splitting;nanoparticles;hot-matrix;

Podatki

Jezik:	Angleški jezik
Leto izida:	2017
Tipologija:	1.12 - Objavljeni povzetek znanstvenega prispevka na konferenci
Organizacija:	UNG - Univerza v Novi Gorici
UDK:	53
COBISS:	4927483
Št. ogledov:	5218
Št. prenosov:	0
Ocena:	0 (0 glasov)
Metapodatki:

Ostali podatki

URN:	URN:SI:UNG
Vrsta dela (COBISS):	Delo ni kategorizirano
Strani:	Str. 128
ID:	10869495