diplomsko delo
Žan Ferčak (Avtor), Blaž Karpe (Mentor)

Povzetek

V sklopu diplomskega dela smo z metodo tranzientnega planarnega toplotnega vira (Hot Disk TPS 2200) v skladu z mednarodnim standardom ISO 22007 opravili meritve toplotnih lastnosti dveh vrst emajlov, ki se uporabljata v industriji bele tehnike. Ker direktnih meritev toplotnih lastnosti emajlirane jeklene pločevine nismo mogli izvesti, smo vzorce emajlov pripravili tudi v obliki debelih plasti. Rezultati, ki smo jih pridobili z meritvami toplotnih lastnosti debelih plasti, so v okviru pričakovanih vrednosti za toplotne lastnosti emajlov, ugotavljamo pa, da ima velik vpliv na toplotne lastnosti dosežena gostota emajlirane plasti. Vzorce emajlirane pločevine smo metalografsko pripravili in analizirali z vrstično elektronsko mikroskopijo (SEM) in optično mikroskopijo (OM). Ugotavljamo, da je plast analiziranih emajlov večfazna, saj je sestavljena iz amorfnih področji z različno kemično sestavo, kristalnih faz in por. Iz mikrokemične analize (SEM-EDS) prahov emajlov pa je razvidno, da določene kristalne faze v plasti emajla na jekleni pločevini izvirajo že iz samega postopka priprave prahov emajlov. Iz mikrokemične analize (SEM-EDS) fazne meje jeklo - emajl je razvidno, da potekajo med žganjem emajla na določenih mestih fazne meje tudi kemične reakcije, pri čemer kobalt difundira v jeklo. Izvedli smo tudi oceno vpliva toplotne prevodnosti emajlirane plasti na toplotno prehodnost emajlirane jeklene pločevine.

Ključne besede

toplotne lastnosti;metoda TPS;hot disk;emajli;emajlirana pločevina;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL NTF - Naravoslovnotehniška fakulteta
Založnik: [Ž. Ferčak]
UDK: 669
COBISS: 1716831 Povezava se bo odprla v novem oknu
Št. ogledov: 1319
Št. prenosov: 563
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: thermal properties of enamels and enamelled metal sheets
Sekundarni povzetek: In the course of the diploma work we performed measurements of the thermal properties of two enamel grades, used for kitchen appliances, by transient plane heat source method (Hot Disk TPS 2200) in accordance with the international standard ISO 22007. Since we could not perform direct measurements of the thermal properties of enameled steel sheets, samples of enamels were also prepared in the form of thick layers. The results obtained from the measurements of the thick layers are within the expected values of the enamels thermal properties. However, it has been established, that the density of the enamel layer has a significant effect on the thermal properties. The samples of the enameled steel sheet were metallographically prepared and analyzed by scanning electron microscopy (SEM-EDS) and optical microscopy (OM). We found out that the layer of analyzed enamels has multiphase structure, consisting of amorphous regions with different chemical composition, crystalline phases and pores. From the microchemical analysis results of the enamel powders it can be seen, that certain crystalline phases in the enameled layer originate from the process of preparing enamel powders. From the microchemical analysis (SEM-EDS) of the steel – enamel phase boundary, it is evident that chemical reactions occur during the firing of the enamel at certain points on the phase boundary, whereby the cobalt diffuses into the steel. An assessment of the influence of enamel layer thermal conductivity on the thermal transmittance of enameled steel sheet is also calculated.
Sekundarne ključne besede: thermal properties;TPS method;hot disk;enamels;enameled steel sheet;
Vrsta dela (COBISS): Diplomsko delo/naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Naravoslovnotehniška fak. , Odd. za materiale in metalurgijo
Strani: VI, 37 f.
ID: 10920878