diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo
Bojan Tomšič (Avtor), Damjan Klobčar (Mentor)

Povzetek

Dodajalne tehnologije so vse bolj razširjene zaradi svojih prednosti, saj omogočajo izdelavo kompleksnih oblik izdelkov. Postopek je v veliko primerih hitrejši od konvencionalnih postopkov obdelave izdelkov ter z njim zmanjšamo stroške odpadnega materiala. Aluminijeve zlitine so začele zaradi svojih mehanskih lastnosti vse bolj nadomeščati jeklo in ostale materiale, saj omogočajo dobro razmerje med trdnostjo in težo. V diplomski nalogi je predstavljena raziskava navarjanja aluminijeve zlitine AlSi5 s postopkom navarjanja MIG. Preučeni so varilni parametri, ki najbolj vplivajo na kakovost navarjenega izdelka pri navarjanju v obliki sten in zaključenih navarov. Prav tako so preučeni tudi vplivi prvega navara, začetkov navarjanja in prehodov navarov na višjo plast izdelka. Na podlagi ugotovljenih optimalnih parametrov je bil navarjen končni izdelek. Kot rezultat dela je dokazano, da je neprekinjeno navarjanje aluminijeve zlitine AlSi5 po postopku MIG uspešno, ob tem pa so z vzorci potrjeni izbrani optimalni parametri navarjanja. Dokazan je tudi vpliv visoke toplotne prevodnosti AlSi5. Preizkušene so delne rešitve za zmanjšanje vpliva te lastnosti materiala na navarjanje.

Ključne besede

diplomske naloge;dodajalne tehnologije;aluminijeve zlitine;AlSi5;WAAM;aluminij;MIG;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FS - Fakulteta za strojništvo
Založnik: [B.Tomšič]
UDK: 621.791.75:669.715(043.2)
COBISS: 16329755 Povezava se bo odprla v novem oknu
Št. ogledov: 777
Št. prenosov: 248
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Wire and arc additive manufacturing of aluminium alloys AlSi5
Sekundarni povzetek: Additve manufacturing technologies are becoming increasingly widespread due to their advantages, as they enable the production of complex forms of products and in many cases the process is faster than conventional processes. They also reduce the cost of material waste. Aluminum alloys are increasingy replacing steel and other materials due to their mechanical properties as they have good strenght to weight ratio. In this diploma thesis the development of additive manufacturing of aluminium alloy AlSi5 with the MIG process is presented. This thesis is a study of welding parameters, which have the greatest influence on the quality of the manufactured walls and circle closed shapes. It also contain the research of influences of the first layer, the beginnings of weld and shifts on higher layer level. Result of this research is the final product, which is made with the most suitable welding parameters. This research confirms possibility of continuous additive manufacturing of aluminium alloy AlSi5 with MIG welding technology and also the selected optimal parameters. The influence of high thermal conductivity of AlSi5 for additive manufacturing was also proven and partial solutions to resolve this issue were tested.
Sekundarne ključne besede: additive manufacturing;aluminium alloys;AlSi5;WAAM;aluminium;MIG;
Vrsta dela (COBISS): Diplomsko delo/naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Fak. za strojništvo
Strani: XXII, 56 str.
ID: 10956714
Priporočena dela:
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo
, zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo
, ni podatka o podnaslovu
, ni podatka o podnaslovu
, zaključna naloga Razvojno raziskovalnega programa I. stopnje Strojništvo