diplomsko delo
Rok Lužnik (Avtor), Milan Šernek (Recenzent), Sergej Medved (Mentor)

Povzetek

Namen tega diplomskega dela je bil izdelati lesni ploščni kompozit iz lesnih ostankov - skobljancev. Cilj je bil izdelati ploščo podobne strukture, kot jo lahko vidimo pri OSB plošči. Kot surovino smo si izbrali lesne skobljance, ki so bili večinoma izdelani iz lesa iglavcev (ostanki mizarskih obratov). Zlepili smo jih v plošče dimenzije 300 cm x 300 cm in debeline 8 mm. Izdelali smo dve vrsti plošč s tremi različnimi gostotami (prve z večjimi gradniki v zunanjem sloju in druge z večjimi gradniki v srednjem sloju). Določili smo gostoto, vlažnost, debelinski nabrek in vpijanje vode ter upogibno in razslojno trdnost. Boljše upogibne trdnosti smo dosegli pri ploščah, kjer smo v zunanjem sloju uporabili večje gradnike, medtem ko je bila višja razslojna trdnost ugotovljena pri ploščah z večjimi gradniki v srednjem sloju.

Ključne besede

lesni ploščni kompozit;OSB;skobljanci;upogibna trdnost;razslojna trdnost;debelinski nabrek;vpijanje vode;gostota;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL BF - Biotehniška fakulteta
Založnik: [R. Lužnik]
UDK: 630*862
COBISS: 3117449 Povezava se bo odprla v novem oknu
Št. ogledov: 733
Št. prenosov: 238
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Planer shavings as a constituent for wood-based composite
Sekundarni povzetek: The purpose of this B. Sc. thesis was to make a wood-based composite from wood residue called wood chips. The aim was to produce a panel with a structure similar to OSB panel. The raw material that we chose was carpentry residue: conifer' planer shavings. We pressed them into panels of 300 x 300 cm and 8 mm thick. We made two kinds of panels with three different densities (the first with bigger particles in the outer layer, and second with bigger particles in the middle layer). We then determined the density, moisture, thickness swelling, water absorption, bending strength, and delamination strength. We concluded that we were able to achieve better bending strength in panels with bigger particles in the outer layer, while the delamination strength was higher in panels with bigger particles in the middle layer.
Sekundarne ključne besede: wood panel composite;OSB;planer shavings;bending strength;internal bond;thickness swelling;water absorption;density;
Vrsta dela (COBISS): Diplomsko delo/naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Biotehniška fak., Oddelek za lesarstvo
Strani: VIII, 27 f., [5] f. pril.
ID: 11229761