Izdelava ivernih plošč iz odsluženega lesa

diplomski projekt

Ana Tršar (Avtor), Sergej Medved (Mentor), Miha Humar (Komentor), Milan Šernek (Komentor)

Povzetek

Ugotavljali smo, kako delež recikliranega iverja vpliva na mehanske lastnosti ivernih plošč, na debelinski nabrek in emisijo formaldehida. V laboratorijskih pogojih smo izdelali iverne plošče z 0 %, 33 %, 66 % in 100 % recikliranega materiala. Največjo upogibno trdnost in modul elastičnosti smo ugotovili pri iverni plošči iz 33 % recikliranega materiala. Najmanjšo upogibno trdnost je imela plošča iz 100 % recikliranega, najmanjši modul elastičnosti pa plošča iz 66 % recikliranega materiala. Razslojna trdnost je bila najboljša pri plošči iz 100 % recikliranega, najslabša pa pri plošči z 0 % recikliranega materiala. Najmanjši debelinski nabrek smo ugotovili pri plošči iz 66 % recikliranega, največji debelinski nabrek pa pri plošči z 0 % recikliranega materiala. Najmanjša emisija formaldehida je bila ugotovljena pri plošči iz 33 % recikliranega, največja pa pri plošči iz 0 % recikliranega materiala.

Ključne besede

iverne plošče;recikliranje;mehanske lastnosti;

Podatki

Jezik:	Slovenski jezik
Leto izida:	2014
Tipologija:	2.11 - Diplomsko delo
Organizacija:	UL BF - Biotehniška fakulteta
Založnik:	[A. Tršar]
UDK:	630*862.2
COBISS:	2274953
Št. ogledov:	396
Št. prenosov:	63
Ocena:	0 (0 glasov)
Metapodatki:

Ostali podatki

Sekundarni jezik:	Angleški jezik
Sekundarni naslov:	Production of particle boards from recycled wood
Sekundarni povzetek:	We researched the influence of the proportion of the recycled particles on the mechanical properties of particle boards, thickness swelling and emission of formaldehyde. In laboratory conditions, we made particle boards with a 0 %, 33 %, 66 % and 100 % recycled material. Good flexural strength and modulus of elasticity was found in particle board from 33 % recycled material. The lowest flexural strength had the board made from 100 % recycled material, and the lowest modulus of elasticity had the board from 66 % recycled material. The best internal bond strength had the board from 100 % recycled material, while the board made of 0 % recycled material had the lowest. The minimum thickness swelling was found in the board from 66 % recycled material, the maximum thickness swelling was found in the board with 0 % recycled material. The smallest emission of formaldehyde was detected in the board from 33 % recycled material, the highest in the board from 0 % recycled material.
Sekundarne ključne besede:	chipboard;recycling;mechanical properties;
Vrsta dela (COBISS):	Delo diplomskega projekta/projektno delo
Komentar na gradivo:	Univ. v Ljubljani, Biotehniška fak., Oddelek za lesarstvo
Strani:	IX, 38 f., [6] f. pril.
ID:	11908575