diplomsko delo - visokošolski strokovni študij
Marko Cvek (Avtor), Aleš Straže (Recenzent), Dominika Gornik Bučar (Mentor), Bogdan Šega (Komentor)

Povzetek

Grče zmanjšujejo uporabnost lesa, saj je na mestih grč močno spremenjen potek oz. lokalni naklon lesnih vlaken, zato ima grčav les slabše mehanske lastnosti. V nalogi smo ugotavljali, kakšne so povezave med grčavostjo in mehanskimi lastnostmi lesa ter primerjali različna pravila ocenjevanja grčavosti. Grče smo ocenjevali po pravilih, ki so podana v DIN 4074-1 standardu in BS 4978 standardu. Položaj in velikost grč smo določali na 475 smrekovih in jelovih konstrukcijskih elementih dimenzij 50 mm x 150 mm x 4000 mm. S štiri-točkovnim upogibnim preskusom smo elementom določili globalni modul elastičnosti in upogibno trdnost. Ugotovili smo, da grčavost vpliva na trdnost, da pa je napovedovanje trdnosti samo na podlagi grč dokaj nezanesljivo (r = 0,27 do 0,56). Najzanesljivejše je napovedovanje trdnosti na podlagi ocene grčavosti po pravilih DIN 4074-1 standarda za razvrščanje nosilcev (parameter A; r = 0,56) in na podlagi ocene deleža grč v prerezu nosilca po BS 4978 standardu (parameter tKAR; r = 0,54). Najmanj zanesljiv kriterij za ocenjevanje grč je globina bočnih grč (parameter EBB; r = 0,28). Izkoristek razvrščanja je bil višji pri razvrščanju na podlagi BS 4978 standarda, pri razvrščanju po DIN 4074-1 standardu pa je bil zelo visok delež (87,4 %) prenizko razvrščenih elementov.

Ključne besede

konstrukcijski les;smrekovina;grče;tKAR;trdnost;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL BF - Biotehniška fakulteta
Založnik: [M. Cvek]
UDK: 630*852.12
COBISS: 2592905 Povezava se bo odprla v novem oknu
Št. ogledov: 325
Št. prenosov: 73
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Knot influence on the strength of a spruce and fir structural sawn timber
Sekundarni povzetek: Knots have an adverse effect on the mechanical properties of wood, due to influence on slope of grain, therefore wood can be less suitable for particular use. The purpose of this thesis was to examine the correlation between knots and the mechanical properties of wood and also the evaluation of different knots measuring methods. A comparison of knot measuring methods listed in the DIN 4074-1 and BS 4978 standards was carried out. The knots positions and size were measured on 475 spruce and fir structural elements with the dimension 50 mm x 150 mm x 4000 mm. Then, the global modulus of elasticity and bending strength were determined, by a destructive four-point bending test. It was established that knots affect wood strength; however, predicting wood strength based only on knots is fairly unreliable (r = 0.27 to 0.56). More reliable strength predictions on the base of knots is grading in accordance with the DIN 4074-1 standard rules for beams (parameter A; r = 0.56) and by knot area ratio grading in accordance with the BS 4978 standard (parameter tKAR; r = 0.54). The least reliable criterion is the depth of lateral knots (parameter EEB; r = 0.28). The yield of grading was higher when the knots were evaluated by BS 4978 standard; when using the DIN 4074-1 standard, however, there was too high ratio (87.4%) of underestimated elements.
Sekundarne ključne besede: construction wood;spruce wood;knot;tKAR;strength;
Vrsta dela (COBISS): Diplomsko delo
Komentar na gradivo: Univ. v Ljubljani, Biotehniška fak., Oddelek za lesarstvo
Strani: XIII, 53 str., [10] str. pril.
ID: 11928332