diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo
Matej Likar (Avtor), Damjan Klobčar (Mentor)

Povzetek

Varjenje s trenjem in mešanjem (FSW) je zelo uporabna tehnologija spajanja aluminijevih zlitin. Za izdelavo zvara se material ne segreje do temperature tališča. V okviru diplomske naloge smo raziskovali uporabo FSW varjenja za varjenje prekrivnih zvarnih spojev. Pri varjenju soležnih zvarov je zaradi dimenzijskega ujemanja potrebna predobdelava površin, pri prekrivnih zvarih pa ne. V diplomski nalogi smo raziskali vpliv globine prevaritve na lastnosti prekrivnega zvarnega spoja. Pri tem smo uporabili 6 varilnih orodij z dolžinami čepov od 3,1 mm do 5,7 mm in premeri ram 10 mm in 12 mm. Varilne parametre smo nastavljali tako, da smo na zunaj dosegli čim lepši izgled zvara. Izdelali smo več vzorcev in na njih izvedli natezni preizkus, s katerim smo izmerili maksimalno doseženo silo, silo, pri kateri je prišlo do porušitve, in relativne raztezke, pri katerih sta bili sili izmerjeni. Rezultate nateznih preizkusov smo ustrezno obdelali in jih preučili. Ugotovili smo, da trdnost prekrivnega zvarnega spoja narašča z naraščanjem globine prevaritve. Dolžina čepa varilnega orodja ima na trdnost spoja večji vpliv kot linijski vnos energije.

Ključne besede

diplomske naloge;aluminijeva zlitina AB-44300 in AW-6082 T6;varjenje s trenjem in mešanjem;FSW varjenje;globina prevaritve;prekrivni zvar;natezni preizkus;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FS - Fakulteta za strojništvo
Založnik: [M. Likar]
UDK: 621.791:669.715(043.2)
COBISS: 29484291 Povezava se bo odprla v novem oknu
Št. ogledov: 361
Št. prenosov: 1
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: The influence of penetration depth on joint properties in FSW welding of aluminium alloy in lap joints
Sekundarni povzetek: Friction stir welding (FSW) is a very useful technology for welding of aluminium alloys. This method does not heat the material to its melting point in order to create the weld. In this thesis, the usefulness of FSW for the welding of lap joints was investigated. When welding butt joints, the surfaces must be machined for their fitting, but with the welding of lap joints, that is not necessary. In this research we investigated the influence of weld depth on properties of friction stir welded lap joints. We used 6 different welding tools with tool pin lengths from 3.1 mm to 5.7 mm and shoulder diameters of 10 mm and 12 mm. Welding parameters were set in order to obtain visually good weld joints. We created multiple samples on which we performed tensile testing. We measured ultimate tensile forces, tensile forces at fracture and the strains, at which these forces were measured. The results of tensile testing were processed and studied. We found out that the tensile strength of a lap joint increases with increasing depth of lap weld. The length of tool pin has a bigger impact on tensile strength of the weld than the linear energy input.
Sekundarne ključne besede: aluminium alloy AB-44300 and AW-6082 T6;friction stir welding;FSW;weld depth;lap joint;tensile testing;
Vrsta dela (COBISS): Diplomsko delo/naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 2022-08-31
Komentar na gradivo: Univ. v Ljubljani, Fak. za strojništvo
Strani: XXIV, 68 str.
ID: 12014885
Priporočena dela:
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo
, zaključna naloga univerzitetnega študijskega programa I. stopnje Strojništvo
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
, magistrsko delo