magistrsko delo
Nejc Jan (Avtor), Ida Poljanšek (Recenzent), Marko Petrič (Mentor), Matjaž Pavlič (Komentor)

Povzetek

V primarni predelavi lesa nastajajo večje količine odstranjene drevesne skorje, ki predstavlja pomemben neizkoriščen ostanek. Zato bi jo bilo v prihodnosti smotrno čim bolje izkoristiti, ne samo v energetske namene temveč predvsem v izdelkih z visoko dodano vrednostjo. Utekočinili smo skorjo smreke (Picea abies Karst.) in jo uporabili za pripravo poliuretanskih premazov za les. Skorjo smo utekočinili v glicerolu, zmesi polietilen glikola in glicerola ter v etilen glikolu. Pri nanosu se je najbolje obnesel premaz iz skorje, utekočinjene v zmesi polietilen glikola in glicerola. Poleg premaza iz skorje, utekočinjene v zmesi polietilen glikola in glicerola, smo za primerjavo okarakterizirali tudi komercialni poliuretanski premaz. Vse teste smo opravili po standardnih postopkih. Rezultati so pokazali nekoliko boljše lastnosti premaza iz utekočinjene drevesne skorje od lastnosti komercialnega poliuretanskega premaza, vendar na račun visokega deleža izocianata v premazu.

Ključne besede

drevesna skorja;utekočinjenje;premazi za les;lastnosti premazov;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.09 - Magistrsko delo
Organizacija: UL BF - Biotehniška fakulteta
Založnik: [N. Jan]
UDK: 630*829.1
COBISS: 2133897 Povezava se bo odprla v novem oknu
Št. ogledov: 330
Št. prenosov: 41
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Synthesis and characterization of polyurethane coatings from liquefied bark
Sekundarni povzetek: Primary wood processing results in formation of large amounts of removed bark, representing an important unused residue. In future, it would be more reasonable to use bark not only for energetic purposes, but above all in high added value products. Norway spruce (Picea abies Karst.) bark was liquefied and applied for preparation of polyurethane wood coatings. The bark was liquefied in glycerol, the mixture of polyethylene glycol and glycerol, and in ethylene glycol. The best results were obtained using the bark liquefied in the mixture of polyethylene glycol and glycerol. Just to compare, in addition to this coating, commercial polyurethane wood coating was also characterised. All characterisation tests were performed according to standard procedures. Compared to the properties of the commercial polyurethane finish, the results exhibited somewhat better properties of the liquefied bark based coating, due to higher content of isocyanate.
Sekundarne ključne besede: bark;wood liquefaction;wood coatings;characteristics of coatings;