magistrsko delo
Peter Poles (Avtor), Urška Šebenik (Mentor), Marjan Marinšek (Član komisije za zagovor), Aleš Ručigaj (Član komisije za zagovor)

Povzetek

V tem magistrskem delu je bila raziskana možnost sintetiziranja cenovno ugodne nenasičene poliestrske smole z uporabo diciklopentadiena prek Diels-Alderjeve reakcije za abrazijsko odporne poliestrske kompozite. Ta smola je bila primerjana s smolo s tetrahidroftalnim anhidridom in smolo z izoftalno kislino. Smole so bile okaraterizirane s FT-IR in NMR spektroskopijo. Termične lastnosti so bile določene z DSC-analizo. Mehanske lastnosti so bile določene s tritočkovnim upogibnim testom in HDT-testom. Abrazijska odpornosti je bila testirana s Taber abraserjem. Ugotovljeno je bilo, da je rezultat abrazijske odpornosti smole s diciklopentadienom boljši od smole z izoftalno kislino, a slabši od rezultata smole s tetrahidroftalnim anhidridom. Z ekonomskega vidika je smola z diciklopentadienom cenejša od smole s tetrahidroftalnim anhidridom zaradi cene surovin. Proces sinteze se bistveno ne razlikuje, zato ne vpliva na ceno končnega proizvoda.

Ključne besede

polimeri;polimerni materiali;poliester;nenasičene poliestrske smole;kompoziti;abrazija;cena;termične lastnosti;mehanske lastnosti;magistrska dela;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.09 - Magistrsko delo
Organizacija: UL FKKT - Fakulteta za kemijo in kemijsko tehnologijo
Založnik: [P. Poles]
UDK: 678.674(043.2)
COBISS: 43444483 Povezava se bo odprla v novem oknu
Št. ogledov: 482
Št. prenosov: 88
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Synthesis of a cost efficient unsaturated polyester resin for abrasion resistance polyester composites
Sekundarni povzetek: The synthesis of a cost efficient unsaturated polyester resin via Diels Alder reaction with dicyclopentadiene for abrasion resistant composites was examined. Resin with dicyclopentadiene was compared to a resin with tethrahydrophthalic anhydride and a resin with isophthalic acid. Resins were characterised by FT-IR and NMR spectroscopy. Thermal properties were determined by DSC analysis. Mechanical properties were determined by three-point flexular test and HDT test. Abrasion resistance was tested by Taber abrasion test. Results suggested that the resin with dicyclopentadiene has better abrasion resistance in comparison with the resin with isophthalic acid. However, it has worse abrasion resistance than the resin with tethrahydrophthalic anhydride. From economic point of view it can be stated that the resin with dicyclopentadiene is cheaper than the resin with tethrahydrophthalic anhydride. This is due to lower prices of raw materials. Process of synthesis of the two resins is very similar and thus does not affect the price of the resin.
Sekundarne ključne besede: unsaturated polyester resin;abrasion;composite;price;
Vrsta dela (COBISS): Magistrsko delo/naloga
Študijski program: 1000376
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Fak. za kemijo in kemijsko tehnologijo, smer Kemijsko inženirstvo
Strani: 71 str.