Barbara Pulko (Avtor), Jaka Tušek (Avtor), James D. Moore (Avtor), Bruno Weise (Avtor), Konstantin Skokov (Avtor), Oleg Mityashkin (Avtor), Andrej Kitanovski (Avtor), Chiara Favero (Avtor), Peter Fajfar (Avtor), Oliver Gutfleisch (Avtor), Anja Waske (Avtor), Alojz Poredoš (Avtor)

Povzetek

We report the processing, analysis and testing of magnetocaloric composite materials consisting of La-Fe-Co-Si particles of various size fractions and a polymer matrix. All of the composites have working temperatures close to room temperature. The composites were pressed into thin plates, a geometry favorable for testing the composites in an active magnetic regenerator (AMR). In order to investigate the influence of particle size and binder type (epoxy), eight different epoxy-bonded La-Fe-Co-Si plates were made and analyzed. We found that the higher filling factor that can be achieved by using a mixture of several particle size fractions has beneficial influence on the thermal conductivity. Tests in the AMR revealed that a maximum temperature span of approximately T=10 K under magnetic field change of 0H=1.15 T can be obtained at no cooling load conditions. The stability of the measured T values and the mechanical integrity of sample after cyclic application of a magnetic field have been monitored for 90,000 cycles and showed no significant changes. We therefore conclude that epoxy-bonded La-Fe-Co-Si magnetocaloric composites have good magnetocaloric properties at low material-processing costs and hence represent a competitive way to produce magnetocaloric materials to be used in AMR.

Ključne besede

magnetocaloric effect;magnetic refrigeration;La-Fe-Co-Si;active magnetic regenerator;epoxy;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UL FS - Fakulteta za strojništvo
UDK: 621.565.8:697.97:620.1(045)
COBISS: 13703963 Povezava se bo odprla v novem oknu
ISSN: 0304-8853
Št. ogledov: 295
Št. prenosov: 194
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarne ključne besede: magnetokalorični efekt;procesiranje materialov;magnetokalorični material;magnetno hlajenje;
Vrsta dela (COBISS): Članek v reviji
Konec prepovedi (OpenAIRE): 2016-09-02
Strani: str. 65-73
Zvezek: ǂVol. ǂ375
Čas izdaje: Feb. 2015
DOI: 10.1016/j.jmmm.2014.08.074
ID: 12794844
Priporočena dela:
, ni podatka o podnaslovu
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
, ǂa ǂnovel approach based on indirect measurements using artificial neural networks