magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
Klemen Pernat (Avtor), Roman Šturm (Mentor)

Povzetek

Magnezijeve zlitine za gnetenje so zaradi nizke specifične gostote zanimive za uporabo v avtomobilski industriji. Za te izdelke je pomembna visoka trajna dinamična trdnost, to lahko izboljšamo z mehanskim utrjevanjem površine. Eden od možnih postopkov je kavitacijsko utrjevanje. V magistrskem delu smo določili vpliv parametrov kavitacijskega utrjevanja magnezijeve zlitine AZ80, ki ima 8,5% Al in 0,5% Zn (masni delež). Zlitina je bila v topilno žarjenem stanju (24 h pri 420 °C) in v staranem stanju (dodatno 8 h pri 250 °C). Vzorce smo utrjevali z različnimi intenzitetami obdelave, ki so se povečevale od 1 s/mm do 20 s/mm. Vrednotili smo naslednje lastnosti: mikrotrdoto, zaostale napetosti, hrapavost, korozijsko odpornost in mikrostrukturo. Vrednosti meritev smo primerjali z osnovnim materialom, tako smo lahko določili globino modificiranega površinskega sloja. Opazovali smo tudi prisotnost erozije materiala in nastanka razpok pri večjih intenzitetah kavitacijskega utrjevanja.

Ključne besede

magistrske naloge;kavitacijsko utrjevanje;magnezijeve zlitine;mikrostruktura;umetno staranje;mikrotrdota;zaostale napetosti;korozijska odpornost;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.09 - Magistrsko delo
Organizacija: UL FS - Fakulteta za strojništvo
Založnik: [K. Pernat]
UDK: 620.193.16:669.721.5(043.2)
COBISS: 78135811 Povezava se bo odprla v novem oknu
Št. ogledov: 571
Št. prenosov: 102
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Cavitation peening of AZ80 magnezium alloy
Sekundarni povzetek: Wrought magnesium alloys are interesting for the automotive industry due to their low specific density. Fatigue strenght is important for this components. Fatigue strenght of components can be improved with mechanical surface hardening. One of the possible surface hardening processes is cavitation peening. In the master's thesis, the influence of cavitation peening parameters on solution treated (24 h at 420 °C) and solution treated aged (after that 8 h at 250 °C) samples of magnesium alloy AZ80, which has 8,5% Al and 0,5% Zn (mass fraction), was determined. The samples were hardened with different peening intensities, which increased from 1 s/mm to 20 s/mm. The following properties were evaluated: micro-hardness, residual stresses, roughness, corrosion resistance and microstructure. The values were compared with the base material and the depth of the modified surface layer was determinated. We also observed the presence of material erosion and the formation of cracks at higher intensities of cavitation peening.
Sekundarne ključne besede: master thesis;cavitation peening;microstructure;artificial aging;hardness;residual stresses;corrosion resistance;
Vrsta dela (COBISS): Magistrsko delo/naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. Ljubljana, Fak. za strojništvo
Strani: XXIV, 73 str.
ID: 13285834
Priporočena dela:
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
, zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program
, ni podatka o podnaslovu
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo