diplomsko delo
Špela Črv (Avtor), Igor Plazl (Mentor)

Povzetek

V šaržnem reaktorju z reciklom smo izvedli teste aktivnosti imobiliziranih fotokatalizatorjev TiO2 in plazmonskih fotokatalizatorjev Au/TiO2 za oksidativno razgradnjo raztopljenega bisfenola A (BPA). Kot osnovni material za fotokatalizatorje smo uporabili komercialno dostopne nanodelce TiO2, na katere smo s pomočjo mokre impregnacije nanesli 1 ut. % Au. Oksidativno razgradnjo smo izvedli pri treh različnih hitrostih pretoka ob osvetljevanju z ultravijolično (UV) in vidno (VIS) pri dveh vrstah fotokatalizatorjev, TiO2 in Au/TiO2. Vsak tip fotokatalizatorja je bil imobiliziran na dva načina: z nanosom s potapljanjem (angl. dip coater) ali z nanosom z vrtenjem (angl. spin coater). Učinkovitost oksidativne razgradnje BPA smo spremljali s pomočjo tekočinske kromatografije visoke ločljivosti (angl. high precision liquid cromatography, HPLC) z UV diodnim detektorjem. Najboljšo razgradnjo smo dosegli s fotokatalizatorjem Au/TiO2, ki je bil nanešen z nanosom z vrtenjem ob osvetljevanju z UV svetlobo in pretokom 60 mL/min. Relativna koncentracija BPA je padla za 52,4 %. Stopnjo mineralizacije BPA smo določili s pomočjo analize celotnega organskega ogljika (angl. total carbon analysis, TOC). Ta je prav tako bila najvišja pri oksidativni razgradnji s fotokatalizatorjem Au/TiO2, ki je bil nanešen z nanosom z vrtenjem ob osvetljevanju z UV svetlobo in pretokom 60 mL/min. Odstotek celotnega odstranjenega organskega ogljika je bil 51 %.

Ključne besede

heterogena fotokataliza;fotokatalizatorji;titanov dioksid;zlato;bisfenol A;oksidativna razgradnja BPA;vidna svetloba;diplomska dela;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FKKT - Fakulteta za kemijo in kemijsko tehnologijo
Založnik: [Š. Črv]
UDK: 66.02:544.526.5(043.2)
COBISS: 81790979 Povezava se bo odprla v novem oknu
Št. ogledov: 244
Št. prenosov: 38
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Optimization of heterogeneous photocatalysis in a batch reactor with recycling
Sekundarni povzetek: Activity tests of immobilized TiO2 photocatalysts and Au/TiO2 plasmon photocatalysts for oxidative degradation of dissolved bisphenol A (BPA) were performed in a batch reactor with recirculation. Commercially available TiO2 nanoparticles were used as the base material for the photocatalysts, to which 1 wt. % Au was added by wet impregnation. Oxidative degradation was performed at three different flow rates under ultraviolet (UV) and visible (VIS) light on two types of immobilized photocatalysts, TiO2 and Au/TiO2. Each type of photocatalyst was immobilized in two ways, either by dip coater or spin coater. The efficiency of oxidative degradation of BPA was monitored using high precision liquid cromatography (HPLC) with a UV diode detector. The best degradation was achieved with spin coater immobolized Au/TiO2 photocatalyst under UV light and a flow rate of 60 mL/min. The relative concentration of BPA fell by 52.4%. The degree of BPA mineralization was determined using total carbon analysis (TOC). The highest percentage of total organic carbon removed was 51 % and was also achieved with oxidative degradation of BPA with spin coater immobolized Au/TiO2 photocatalyst under UV light and a flow rate of 60 mL/min.
Sekundarne ključne besede: heterogenous photocatalysis;titanium dioxide;gold;bisphenol A;visible light;
Vrsta dela (COBISS): Diplomsko delo/naloga
Študijski program: 1000372
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Fak. za kemijo in kemijsko tehnologijo, UNI Kemijsko inženirstvo
Strani: 30 str.
ID: 13356508