Merjenje zaostalih napetosti v zvarih na dupleks nerjavnih jeklih
zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program
Povzetek
Zaostale napetosti se pojavljajo pri skoraj vseh proizvodnih procesih, kjer v material vnašamo energijo in vplivajo na življenjsko dobo izdelka. Zaključna naloga temelji na teoretičnem pregledu in sicer se osredotoča na zaostale napetosti, ki nastanejo v zvarih na dupleks nerjavnih jeklih. Obravnavani bodo varjeni kvadratni in H-profili iz vitkega dupleks nerjavečega jekla. Meritve natezni in tlačnih napetosti so bile opravljene z nedestruktivno metodo nevtronske difrakcije, Izvedena je bila analiza trdote in mikrostrukturna karakterizacija z optično mikroskopijo in difrakcijo s povratnim sipanjem elektronov. S tem je bil ugotovljen volumenski delež posamezne faze in preračunane zaostale napetosti. Največje natezne zaostale napetosti varjenih kvadratnih profilov so bile opažene v bližini zvarov, in sicer za vzorec S-1 in S-2. Pri H-profilu pa so bile največje zaostale napetosti opažene na sredini razpona stranskih plošč in na obeh koncih prirobnice.
Ključne besede
diplomske naloge;varjenje;zvar;TIG varjenje;dupleks nerjavna jekla;mikrostruktura;zaostale napetosti;nevtronska in rentgenska difrakcija;mehanske lastnosti;
Podatki
| Jezik: | Slovenski jezik |
|---|---|
| Leto izida: | 2022 |
| Tipologija: | 2.11 - Diplomsko delo |
| Organizacija: | UL FS - Fakulteta za strojništvo |
| Založnik: | [K. Muhič] |
| UDK: | 621.791.725(043.2) |
| COBISS: |
137043203
|
| Št. ogledov: | 371 |
| Št. prenosov: | 55 |
| Ocena: | 0 (0 glasov) |
| Metapodatki: |
|
Ostali podatki
| Sekundarni jezik: | Angleški jezik |
|---|---|
| Sekundarni naslov: | Residual stress measurments of lean duplex stainless steel welded sections |
| Sekundarni povzetek: | Residual stresses appear in almost all production processes where energy is introduced into the material and affect the product's lifetime. The final thesis is based on a theoretical review and focuses on residual stresses that occur in duplex stainless steel welds. Welded square and H-profiles made of slender duplex stainless steel will be considered. Tensile and compressive stress measurements were performed using the non-destructive neutron diffraction method. Hardness analysis and microstructural characterization were performed using optical microscopy and electron backscatter diffraction. With this, the volume fraction of each phase and the calculated residual voltage were determined. The highest tensile residual stresses of the welded square profiles were observed near the welds, namely for sample S-1 and S-2. For the H-profile, however, the highest residual stresses were observed at the mid-span of the side plates and at both ends of the flange. |
| Sekundarne ključne besede: | thesis;welding;weld;TIG welding;duplex stainless steel;microstructure;mechanical properties; |
| Vrsta dela (COBISS): | Zaključna naloga |
| Študijski program: | 0 |
| Konec prepovedi (OpenAIRE): | 1970-01-01 |
| Komentar na gradivo: | Univ. v Ljubljani, Fak. za strojništvo |
| Strani: | XIV, [29] f. |
| ID: | 16901270 |
Priporočena dela:
Merjenje zaostalih napetosti v zvarih na dupleks nerjavnih jeklih
2022,
zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program
Zaostale napetosti v zvarih na aluminijevi zlitini 7075
2018,
diplomska naloga visokošolskega strokovnega študijskega programa I. stopnje strojništvo
Odkrivanje korenskih razpok v zvarih nerjavnih jekel z ultrazvočno metodo
2021,
diplomska naloga
Določitev varilne tehnologije za reaktor s hladilno polcevno kačo
2006,
diplomsko delo visokošolskega strokovnega študijskega programa
Optimizacija kombiniranega varjenja debelostenske nerjavne cevi
2020,
diplomsko delo