zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program
Gal Klenovšek (Avtor), Uroš Trdan (Mentor), Damjan Klobčar (Komentor)

Povzetek

Naloga primerja karakteristiko lomnih površin pri nateznem in udarnem lomu materiala, glede na smer oblikovno obločnega navarjanja žice aluminijeve zlitine - AlSi5. Uporabljeni vzorci so bili izrezani iz navarjene stene in nato obremenjeni vzporedno oziroma pravokotno na smer navarjenih plasti. SEM (angl. SEM - scanning electron microscope) analizo lomnih površin smo izvedli z elektronskim vrstičnim mikroskopom visoke globinske ostrine. Pri analizi smo preverjali mikrostrukturne značilnosti prelomne površine. Rezultati analize so potrdili žilavi prelom materiala neodvisno od tipa preizkusa in orientacije preizkušanca glede na smer izgradnje izdelka. Bistvenih razlik med vzorci izrezanih vzporedno in pravokotno na dodajalne plasti ni bilo zaznati. Ostala opažanja med posameznimi vzorci so, da smo pri vzorcih lomljenih z udarnim preizkusom zaznali 200% višjo pogostost in 164% večji premer plinske poroznost kot pri vzorcih izdelanih za natezni preizkus. Povprečni premer plinskih por na prelomnih površinah je po izvedenem nateznem preizkusu znašal 39,49 ± 13,12 µm, po udarnem preizkusu pa 65,00 ± 22,41 µm. Razlika je posledica različnega načina izdelave preizkušancev ter izvedbe samega testa. Za izdelavo stene, iz katere so bili izrezani preizkušanci na udarni preizkus, so se za doseganje potrebne širine preizkušanca uporabili polnilni vari, ki so v vzorec vnesli višjo količino nečistoč in povečali izpostavljenost vara atmosferi.

Ključne besede

diplomske naloge;WAAM;obločno navarjenje;SEM analiza;AlSi5;kovinski prelomi;natezni test;udarni test;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FS - Fakulteta za strojništvo
Založnik: [G. Klenovšek]
UDK: 621.791.75:669.715:539.42(043.2)
COBISS: 163397379 Povezava se bo odprla v novem oknu
Št. ogledov: 75
Št. prenosov: 9
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Analysis of fracture surfaces of WAAM alloy AlSi5
Sekundarni povzetek: This document compares the fracture surface characteristics of tensile and impact fractures in a material, based on the direction of wire arc additive manufactured aluminum alloy wire - AlSi5. The specimens used were cut from a welded wall and subsequently loaded parallel and perpendicular to the direction of the welded layers, respectively. Scanning electron microscope (SEM) analysis of the fracture surfaces was conducted using a high depth of field scanning electron microscope. The microstructural characteristics of the fracture surfaces were examined. The analysis results affirmed the toughness of the fractured material, regardless of the test type or the orientation of the test piece concerning the build direction of the product. No significant differences were observed between specimens cut parallel and perpendicular to the welding layers. Additional observations among individual specimens reveal that specimens fractured by impact testing exhibited a 200% higher frequency and 164% larger diameter of gas pores compared to specimens fractured by tensile testing. Consequently, the average diameter of gas pores on the fractured surfaces measured 39.49 ± 13.12 µm after the tensile test and 65.00 ± 22.41 µm after the impact test. This discrepancy can be attributed to the distinct manner in which the test specimens were manufactured and tested. The wall from which the impact test specimens were extracted utilized filler welds to attain the necessary specimen width, which led to a greater introduction of impurities into the specimen and heightened exposure of the weld to the atmosphere.
Sekundarne ključne besede: thesis;WAAM;Arc welding;SEM analysis;AlSi5;metal fractures;tensile test;impact test;
Vrsta dela (COBISS): Zaključna naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Fak. za strojništvo
Strani: XI, 37 f.
ID: 19867826
Priporočena dela:
, zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo - Projektno aplikativni program
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
, zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo - Projektno aplikativni program