magistrsko delo
Jaka Strohsack (Avtor), Tomaž Mertelj (Mentor)

Povzetek

Z ultrahitro časovno ločljivo optično spektroskopijo smo raziskovali vpliv stika kobalta z različnimi organskimi molekulskimi polprevodniki na magnetno anizotropijo v tankih filmih kobalta. Poleg vpliva molekul smo za primerjavo raziskovali tudi vpliv površinske oksidacije kobalta. Med vzorci z različnimi molekulami različnih oblik nismo opazili velikih razlik v obnašanju. Ugotovili smo, da so molekule povzročile močno povečanje magnetne anizotropije v ravnini filmov pod temperaturo $\sim$170 K. Prav tako se je povečala njena nehomogenost. V vzorcu s kobaltovim oksidom smo pod temperaturo $\sim$100 K prav tako opazili povečanje ravninske magnetne anizotropije, ki pa je bilo manjše kot v vzorcih z molekulami.

Ključne besede

tanki filmi;kobalt;ultrahitra časovno ločljiva optična spektroskopija;magnetna anizotropija;spinski stik;organski polprevodniki;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.09 - Magistrsko delo
Organizacija: UL FMF - Fakulteta za matematiko in fiziko
Založnik: [J. Strohsack]
UDK: 538.9
COBISS: 164348931 Povezava se bo odprla v novem oknu
Št. ogledov: 7
Št. prenosov: 1
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Influence of metal-organic interface on the magnetic anisotropy in Co thin films
Sekundarni povzetek: By means of the ultrafast time-resolved optical spectroscopy we investigated the effect of different organic molecular semiconductors on the magnetic anisotropy of cobalt thin films as a consequence of forming a ferromagnetic-metal/organic-semiconductor spinterface. In addition to the molecules, the effect of natural cobalt surface oxidation was also investigated for comparison. We did not find large differences in the behavior of the samples containing molecules of different geometries. The molecules were found to significantly increase the in-plane magnetic anisotropy of the films below the temperature of $\sim$170 K. Additionally, the magnetic anisotropy inhomogeneity increased. The in-plane magnetic anisotropy also increased in the naturally oxidized sample below the temperature of $\sim$100 K. The increase was much smaller then in samples with organic molecules.
Sekundarne ključne besede: thin films;cobalt;ultrafast time-resolved optical spectroscopy;magnetic anisotropy;spinterface;organic semiconductors;
Vrsta dela (COBISS): Magistrsko delo/naloga
Študijski program: 0
Komentar na gradivo: Univ. v Ljubljani, Fak. za matematiko in fiziko, Oddelek za fiziko
Strani: 58 str.