diplomsko delo (visokošolski strokovni študij)
Povzetek
Na ravnovesno vlažnost plošč vpliva več dejavnikov, med njimi tudi debelina in tip plošče oziroma vrsta lepila. Pri poizkusu smo imeli 4 različne tipe ploščč iz njih smo izžagali 24 vzorčkov dimenzij 50 mm X 50 mm. Te smo najprej navlaževali, in sicer v klimah z relativno zrčno vlažnostjo 34 %, 65 %, 75 %, 90 % in 98 % do konstantne mase. Zatem smo postopek obrnili in jih pričeli sušiti. Imeli smo iste klime kot pri navlaževanju. Na koncu smo jih dali še v sušilnik s 103 +- 2 °C. Opazovali smo spremembe mase in nabreka. Najbolje so se obnesli vzorčki P5, zlepljeni z melamin-formaldehidnim lepilom. Tudi vzorčki OSB3, zlepljeni z izocianatnim lepilom, so se dobro obnesli do relativne zračne vlažnosti 90 %, nato pa se je nabrek močno povečal. Pri debelejših in tanjših vzorčkih P2, ki so bili zlepljeni z urea-formaldehidnim lepilom, so se bolje obnesli tanjši vzorčki.
Ključne besede
iverne plošče;higroskopnost;lepilo;nabrek;
Podatki
Jezik: |
Slovenski jezik |
Leto izida: |
2007 |
Izvor: |
Ljubljana |
Tipologija: |
2.11 - Diplomsko delo |
Organizacija: |
UL BF - Biotehniška fakulteta |
Založnik: |
[J. Soršak] |
UDK: |
630*862.2 |
COBISS: |
1492105
|
Št. ogledov: |
1262 |
Št. prenosov: |
287 |
Ocena: |
0 (0 glasov) |
Metapodatki: |
|
Ostali podatki
Sekundarni jezik: |
Angleški jezik |
Sekundarni naslov: |
Sorption and swelling characteristics of particle boards |
Sekundarni povzetek: |
Various factors affect the equilibrium moisture content in particle boards; so as thickness of the board, type of the board, and type of the resin. 4 different types of particle boards were used for our experiment. They were cut into 24 samples; their size was 50 mm X 50 mm. First, samples were moistened in a climate with 34 %, 65 %, 75 %, 90 % and 98 % atmospheric humidity, maintaining the constant weight of the particles. After moistening, the boards were dried using the same climates as before, and then put into a dryer with 103+-2 °C. Changes of weight and swelling were observed. P5 samples glued by melamine-formaldehyde resine turned out to be the best. OSB3 samples glued by isosyanate resin turned out well up to 90 % humidity; then the swelling increased significantly. Among P2 samples glued by urea-formaldehyde resin the thinner samples turned out to be better from the thicker ones. |
Sekundarne ključne besede: |
particle board;hygroscopicity;resin;swelling; |
Vrsta dela (COBISS): |
Diplomsko delo |
Komentar na gradivo: |
Diplomsko delo, Univ. v Ljubljani, Biotehniška fakulteta, Oddelek za lesarstvo |
Strani: |
VIII, 65 f. |
Ključne besede (UDK): |
applied sciences;medicine;technology;uporabne znanosti;medicina;tehnika;agriculture and related sciences and techniques;forestry;farming;wildlife exploitation;kmetijstvo ter sorodne vede in tehnologije;forestry;gozdarstvo;forest products and their utilization;gozdni proizvodi in njihova uporaba; |
ID: |
21085 |