Chodisetti Surya Prakasarao (Avtor), Mitjan Kalin (Avtor), B.V. Manoj Kumar (Avtor)

Povzetek

Friction and wear characteristics of spark plasma sintered SiC-▫$TiB_2$▫ composites in reciprocating sliding contacts are evaluated in terms of ▫$TiB_2$▫ content (0 - 30 vol%), normal load (5, 10 and 15 N) and temperature (25 °C and 600 °C). With increase in TiB2 content, friction increased, and wear decreased. Scanning electron microscopy, atomic force microscopy and Raman spectroscopy studies confirm protective tribo-oxidation in sliding at 600 °C. Effect of wear debris on friction response and wear resistance is emphasised. Wear mechanisms changed from fracture at 25 °C to tribo-oxidation at 600 °C. The presence of ▫$TiB_2$▫ reinforcement helps in enhancing wear resistance of SiC ceramics at room temperature, while formation of oxide layer and cylindrical debris are responsible for less wear at 600 °C.

Ključne besede

SiC;composites;reciprocating sliding;wear;high temperature;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UL FS - Fakulteta za strojništvo
UDK: 539.4
COBISS: 178242307 Povezava se bo odprla v novem oknu
ISSN: 0955-2219
Št. ogledov: 668
Št. prenosov: 18
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarne ključne besede: kompoziti;trenje;obraba;
Vrsta dela (COBISS): Članek v reviji
Konec prepovedi (OpenAIRE): 2025-12-16
Strani: str. 2704-2719
Letnik: ǂVol. ǂ44
Zvezek: ǂiss. ǂ5
Čas izdaje: May 2024
DOI: 10.1016/j.jeurceramsoc.2023.12.055
ID: 22895645