Matjaž Kristl (Avtor), Urška Ostroško (Avtor), Irena Ban (Avtor), Irena Petrinić (Avtor), Janja Stergar (Avtor)

Povzetek

Iron-based magnetic nanoparticles (MNPs) have attracted considerable attention as promising draw solutes in forward osmosis processes due to various advantages. In the present study, magnetite (Fe3O4) nanoparticles (MNPs) with diameters in the range of 12±2 nm were synthesized by applying the coprecipitation method and stabilized using (3-aminopropyl) triethoxysilane (APTES). The amino groups of APTES were further functionalized with various amounts of citric acid (CA) and poly(acrylic acid) (PAA) to achieve higher osmotic pressure. The as-prepared and functionalized nanoparticles were characterized using diferent methods: Fourier-transform infrared spectroscopy (FTIR) confrmed the binding of APTES and CA/PAA on the surface of the MNPs, while the size of the particles was determined by transmission electron microscopy (TEM) and X-ray powder difraction. The isoelectric point, zeta potential, and the particle size in suspension were determined by dynamic light scattering (DLS)/zeta potential measuring system. The amount of free –COOH groups was determined by conductometric titrations. The amount of organic matter (APTES, CA, and PAA) bound on the surface was determined by thermogravimetric analysis (TG), giving results between 7.6% for samples stabilized with APTES only and 17.5% for samples functionalized with APTES+PAA. TG provides a simple and efcient method for determining the amount of organic compounds bound to the surface of MNPs. The osmotic pressure measurements of double-layer coated MNPs provided encouraging results of up to 28 bar, enabling using the samples as draw solutions in an experimental forward osmosis system.

Ključne besede

magnetni nanodelci;magnetiti;citronska kislina;povratna osmoza;magnetic nanoparticles;magnetite;citrit acid;poly(acrylic acid);forward osmosis;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UM FERI - Fakulteta za elektrotehniko, računalništvo in informatiko
Založnik: Springer Link
UDK: 66.02
COBISS: 189345283 Povezava se bo odprla v novem oknu
ISSN: 1588-2926
Št. ogledov: 17
Št. prenosov: 0
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarne ključne besede: magnetni nanodelci;magnetiti;citronska kislina;povratna osmoza;
Vrsta dela (COBISS): Članek v reviji
Strani: 15 str.
Čas izdaje: Published: 15 March 2024
DOI: 10.1007/s10973-024-12983-2
ID: 24720624