diplomsko delo
Andrej Pavlič (Avtor), Manja Kitek Kuzman (Recenzent), Mirko Kariž (Mentor)

Povzetek

Tehnologije tridimenzionalnega tiskanja omogoča izdelavo tako prototipov, končnih izdelkov kot celotnih objektov. Na podlagi računalniškega modela se z dodajanjem materiala v plasteh tvori izdelek brez dodatnih kalupov. Zaradi številnih prednosti se povečuje uporaba 3D tehnologij in z njim poraba materiala, kateremu bi lahko izboljšali ekološki vidik z dodajnem lesa. Namen naloge je bil pripraviti zmes iz lesnih delcev, mavca in lepila, ki bi omogočala tiskanje z ekstrudiranjem. Zmesem, ki so vsebovale različne deleže lesa, mavca in lepila smo izmerili povprečno silo za ekstrudiranje skozi tiskalno šobo. Z izbranimi zmesmi smo 3D natisnili enostavne preskušance, katerim smo izmerili upogibno trdnost in s testiranjem določili vpliv posameznih komponent na lastnosti materiala. Delež lesa v zmesi je povečeval potrebno silo za iztiskanje, medem ko je večja vsebnost lepila to silo zmanjšala. Najvišjo upogibno trdnost 6,7 N/mm² so dosegli preskušanci narejeni iz zmesi 25 % lepila, 22 % lesnih delcev in 53 % mavca. Dodajanje lepila je povečevalo trdnost, medem ko je imel les nasproten učinek. Delež lesa je vplival tudi na izgubo mase in ukrivljenje preskušancev med utrjevanjem/sušenjem. Zaradi skrčka in posedanja materiala med sušenjem je omejena tudi natančnost končnih izdelkov in je ta material bolj primeren za izdelke z manjšo zahtevano natančnostjo oblike.

Ključne besede

tridimenzionalno tiskanje;lesni delci;mavec;lepilo;upogibna trdnost;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL BF - Biotehniška fakulteta
Založnik: [A. Pavlič]
UDK: 630*86: 004.356.2
COBISS: 206735107 Povezava se bo odprla v novem oknu
Št. ogledov: 454
Št. prenosov: 129
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Three-dimensional printing with a mixture of wood particles, plaster and glue
Sekundarni povzetek: Three-dimensional printing technologies enable the production of prototypes, finished products, and even entire buildings. By adding material layer by layer, products are formed directly from a computer model without the need for additional moulds. Due to the many advantages of 3D printing, its use is rapidly increasing, along with the consumption of materials. This growth in material usage could be made more sustainable by incorporating wood into the mix. The purpose of this task was to develop a mixture of wood particles, plaster, and glue that would allow for extrusion-based 3D printing. We tested mixtures with different proportions of wood, plaster, and glue, measuring the average force required for extrusion through the printing nozzle. Using the selected mixtures, we 3D printed simple test pieces, measured their bending strength, and assessed the influence of individual components on the material properties. The results showed that increasing the proportion of wood in the mixture raised the force required for extrusion, while a higher glue content reduced this force. The highest flexural strength, 6.7 N/mm², was achieved by specimens made from a mixture containing 25% glue, 22% wood particles, and 53% plaster. While adding glue increased the strength, the addition of wood had the opposite effect. The proportion of wood also affected the mass loss and the bending of the specimens during hardening. Due to shrinkage and material settling during drying, the accuracy of the finished products is limited, making this material more suitable for products with lower shape accuracy requirements.
Sekundarne ključne besede: 3D printing;wood particles;plaster;glue;bending strength;
Vrsta dela (COBISS): Diplomsko delo/naloga
Študijski program: 0
Komentar na gradivo: Univ. v Ljubljani, Biotehniška fak., Oddelek za lesarstvo
Strani: 1 spletni vir (1 datoteka PDF (VII, 33 str.))
ID: 24956232