magistrsko delo
Luka Kopač (Avtor), Miha Humar (Recenzent), Sergej Medved (Mentor), Boštjan Lesar (Komentor)

Povzetek

Uporaba ivernih plošč za izdelavo pohištva je v današnjem času zelo razširjena, manj pa se uporabljajo v konstrukcijske namene. Eden od razlogov je slaba odpornost ivernih plošč proti gorenju, ki jo lahko izboljšamo z uporabo zaviralcev ognja. Dodatek le-teh ima pogosto negativen vpliv na mehanske lastnosti, poleg tega pa se pri gorenju, zaradi rabe lepil na osnovi formaldehida, še dodatno poveča emisija formaldehida. Raziskovali smo učinkovitost kombinacije citronske kisline in sorbitola kot veziva ter amonijevega dihidrogenfosfata kot zaviralca ognja, na protipožarne in upogibne lastnosti ivernih plošč ter njihovo razslojno trdnost in odpornost na vodo. Poskušali smo izdelati iverno ploščo z najboljšimi lastnostmi protipožarnega delovanja in hkrati s čim manjšim poslabšanjem trdnosti. Z večjim deležem veziva so se lastnosti izboljšale, medtem ko velikost gradnikov ni igrala pomembne vloge. Dodatek amonijevega dihidrogenfosfata je izboljšal odpornost na vodo, ampak imel negativen vpliv na mehanske lastnosti. Najbolj optimalen delež dodanega protipožarnega sredstva je bil 5 %. Pri preizkusu na vroči plošči smo ugotovili večjo izgubo mase pri vzorcih z dodanim amonijevim dihidrogenfosfatom, domnevno zaradi njegovega razpada pri povišani temperaturi. Predvidevamo, da razpadni produkti ščitijo ploščo pred ognjem, kar je bilo razvidno pri izpostavitvi plamenu na robu preizkušanca.

Ključne besede

iverna plošča;citronska kislina;amonijev dihidrogenfosfat;zaviralec ognja;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.09 - Magistrsko delo
Organizacija: UL BF - Biotehniška fakulteta
Založnik: [L. Kopač]
UDK: 630*862.1:843.1
COBISS: 207588867 Povezava se bo odprla v novem oknu
Št. ogledov: 30
Št. prenosov: 6
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: ǂThe ǂeffects of particle size and amount of fire retardant on the properties of formaldehyde-free particleboards
Sekundarni povzetek: The use of particleboards for the manufacture of furniture is very common, but they are used less often for structural purposes. One of the reasons is the poor fire safety of particleboards, which can be improved using fire retardants. However, their addition often has a negative impact on the boards' mechanical properties, and using formaldehyde-based adhesives increases emissions during a fire. The objective was to investigate the efficacy of citric acid and sorbitol as an adhesive and ammonium dihydrogen phosphate as a fire retardant. The properties measured were fire retardancy, MOR, MOE, IB and moisture resistance. In several steps we tried manufacturing a board with the best fire retardant properties with as little deterioration of strength as possible. The properties improved with a higher proportion of binder, while the size of the particles did not play a significant role. The addition of ammonium dihydrogen phosphate improved moisture resistance but had a negative effect on mechanical properties. The optimal proportion of fire retardant was 5 wt%. In the hot plate test a greater mass loss was recorded in samples with added ammonium dihydrogen phosphate, presumably due to its decomposition at elevated temperature. The resulting products seemed to protect boards when exposed to flame impingement on the sample's edge.
Sekundarne ključne besede: particleboard;citric acid;ammonium dihydrogen phosphate;fire retardant;
Vrsta dela (COBISS): Magistrsko delo/naloga
Študijski program: 0
Komentar na gradivo: Univ. v Ljubljani, Biotehniška fak., Oddelek za lesarstvo
Strani: 1 spletni vir (1 datoteka PDF (VI, 40 str.))
ID: 25059876