Subsolidus phase equilibria and the Li[sub]5Nd[sub]4FeO[sub]10 phase in the Li[sub]2O-Nd[sub]2O[sub]3-Fe[sub]2O[sub]3 system

Irena Ban (Avtor), Mihael Drofenik (Avtor), Danilo Suvorov (Avtor), Darko Makovec (Avtor)

Povzetek

A survey of the subsolidus phase equilibria in the system Li2O-Nd2O3-Fe2O3 wasmade at subsolidus temperatures in the range 1000-1050 °C. A ternary phase was identified. The phase is centered on Li5Nd4FeO10, with a cubic lattice a =11.9494 A. The compound melts incongruently at 1105 °C. The magnetic susceptibility was measured in the temperature range 4-300 K. The compound is paramagnetic in the temperature range 150-300 K and follows the Curie-Weiss law. At about TN = 10 K, a long-range magnetic ordering is observed.

Ključne besede

lithium ferrites;differential scanning calorimetry;thermogravimetric analysis;X-ray diffraction;magnetic properties;phase equilibrium;

Podatki

Jezik:	Angleški jezik
Leto izida:	2005
Tipologija:	1.01 - Izvirni znanstveni članek
Organizacija:	UM FKKT - Fakulteta za kemijo in kemijsko tehnologijo
UDK:	546.34
COBISS:	9802006
ISSN:	0025-5408
Št. ogledov:	1803
Št. prenosov:	26
Ocena:	0 (0 glasov)
Metapodatki:

Ostali podatki

Sekundarni jezik:	Angleški jezik
URN:	URN:SI:UM:
Strani:	str. 1856-1863
Letnik:	ǂVol. ǂ40
Zvezek:	ǂiss. ǂ10
Čas izdaje:	2005
ID:	8718316