Jadranka Malina (Avtor), Ivan Samardžić (Avtor), Vladimir Gliha (Avtor)

Povzetek

We study the hydrogen embrittlement and rupture of specimens of high-strength low-alloy steel with weld beads subjected to hydrogenation under the conditions of cathodic polarization. The specimens fail in the heat-affected zone on the boundary between the main metal and the weld bead in the zone of application of the latter and, especially, near its end. This explained by a higher hardness of the metal in this zone caused by the specific features of the temperature field formed in the process of welding.

Ključne besede

varjenje;zvarni spoji;konstrucijska jekla;materiali;razpokanje;vodik;welding;welded joints;materials;structural steel;cracking;hydrogen;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UM FS - Fakulteta za strojništvo
UDK: 621.791.05:539.5
COBISS: 10142486 Povezava se bo odprla v novem oknu
ISSN: 1068-820X
Št. ogledov: 1258
Št. prenosov: 28
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarne ključne besede: varjenje;zvarni spoji;konstrucijska jekla;materiali;razpokanje;vodik;
URN: URN:SI:UM:
Strani: str. 253-258
Letnik: ǂVol. ǂ41
Zvezek: ǂno. ǂ2
Čas izdaje: 2005
ID: 8718368