Merjenje notranjih deformacij v cementnih maltah

diplomsko delo visokošolskega strokovnega študijskega programa

Tadej Fister (Avtor), Andrej Ivanič (Mentor)

Povzetek

V okviru diplomske naloge je bil razvit in izdelan merilec za merjenje volumenskih deformacij v cementni malti. Merilec je omogočal začetek merjenja takoj po vgraditvi v togi brezšivni jekleni kalup valjaste oblike, torej je bilo omogočeno spremljanje razvoja deformacij, ki se razvijejo v prvih urah po zamešanju cementne malte. Meritve so bile opravljene na čisti cementni malti in na malti, kateri je bila dodana kontrolirana količina aeranta. Aerant je bil uporabljen kot sredstvo za nastanek ciljne mikrostrukture cementne malte. Potrjena je bila hipoteza, da stabilizirani zračni mehurčki nudijo neomejen prostor za neovirano in intenzivno rast kristalov CH in etringita na obodu mehurčka in povzročijo volumensko ekspanzijo cementne matrice v začetni fazi hidratacije, ki je bistveno večja, kot pa je ekspanzija malte brez aeranta. V kasnejši fazi hidratacije pa zračni mehurčki vplivajo na intenzivnejše krčenje. Tendenca izmerjenih rezultatov notranjih deformacij, tako ekspanzije kot tudi krčenja, se giblje v skladu z navedbami literature.

Ključne besede

cement;hidratacija;aerant;krčenje;ekspanzija;

Podatki

Jezik:	Slovenski jezik
Leto izida:	2009
Izvor:	Maribor
Tipologija:	2.11 - Diplomsko delo
Organizacija:	UM FGPA - Fakulteta za gradbeništvo, prometno inženirstvo in arhitekturo
Založnik:	[T. Fister]
UDK:	666.9.015.42(043.2)
COBISS:	13696022
Št. ogledov:	2398
Št. prenosov:	145
Ocena:	0 (0 glasov)
Metapodatki:

Ostali podatki

Sekundarni jezik:	Angleški jezik
Sekundarni naslov:	Measurement of internal deformations in cementitious mortars
Sekundarni povzetek:	In the presented diploma thesis the device for measurement of volumetric deformations on cementitious mortars was developed and manufactured. The device enabled starting the measurements immediately after casting of fresh mortars into rigid cylindrical steel molds, which gives a possibility of recording the early-age deformations. Two experimental mortar mixes were used: plain cement mortar and the mortar with addition of air entraining agent (AEA). The addition of AEA caused the formation of the microstructure with finely dispersed air bubbles forming an unlimited space for growth of CH crystals and ettringite. The formation of ettringite and CH crystals is considered as a principal cause of early-age expansion much higher on mortars with AEA. Subsequent shrinkage was found to be also more intense on mortars with AEA. The results of measurements performed in this study are in accordance with findings of literature.
Sekundarne ključne besede:	cement;hydration;air entraining agent;shrinkage;expansion;
URN:	URN:SI:UM:
Vrsta dela (COBISS):	Diplomsko delo
Komentar na gradivo:	Univ. v Mariboru, Fak. za gradbeništvo
Strani:	IX, 41 f.
Ključne besede (UDK):	applied sciences;medicine;technology;uporabne znanosti;medicina;tehnika;chemical technology;chemical and related industries;kemijska tehnologija;kemijske in sorodne industrije;glass industry;ceramics;cement and concrete;industrija stekla;keramika;cement in beton;gypsum;lime and cement industries;hard-setting materials;plasters and compositions;mortar and concrete;industrije mavca;apna in cementa;vezivni materiali;ometi in sestavne zmesi;malta in beton;
ID:	8761579