Lastnosti sušene mikro- in nanofibrilirane celuloze

Vesna Žepič (Avtor), Aleš Hančič (Avtor), Ida Poljanšek (Avtor), Primož Oven (Avtor)

Povzetek

V študiji smo preiskali in analitično ovrednotili morfološke in strukturne lastnosti suhe mikro- (MFC) in nanofibrilirane(NFC) celuloze, ki smo ju pridobili po zračnem sušenju in po sušenju z zamrzovanjem vodnih suspenzij MFC in NFC. Morfološke lastnosti sušene MFC in NFC smo raziskali z vrstično elektronsko mikroskopijo (FE-SEM), strukturne lastnosti pa z infrardečo spektroskopijo (FT-IR). Pri zračnem sušenju vodne suspenzije fibrilirane celuloze nastane prosojen film naključno urejenih fibril, pri sušenju z zmrzovanjem pa fibrilirana celuloza agregira v 80 μm velike grobe praškaste delce. Preiskave z FT-IR niso pokazale razlik med različno sušenimi vzorci fibrilirane celuloze. Uporabljeni metodi sušenja pomembno vplivata na morfologijo suhe MFC in NFC, ne pa tudi na njuno kemijsko strukturo, kar potrjujejo identični FT-IR spektri

Ključne besede

celuloza;MFC;NFC;zračno sušenje;liofilizacija;mikroskopija;spektroskopija;

Podatki

Jezik:	Slovenski jezik
Leto izida:	2013
Tipologija:	1.08 - Objavljeni znanstveni prispevek na konferenci
Organizacija:	UL BF - Biotehniška fakulteta
UDK:	547.458.8
COBISS:	2109833
ISSN:	0024-1067
Št. ogledov:	1435
Št. prenosov:	417
Ocena:	0 (0 glasov)
Metapodatki:

Ostali podatki

Sekundarni jezik:	Angleški jezik
Sekundarni naslov:	Properties of dried micro- and nanofibrillated cellulose
Sekundarni povzetek:	The aim of this study was to investigate and analytically evaluate morphology and structural properties of dried micro-(MFC) and nanofibrillated (NFC) cellulose, obtained after air and freeze drying of aqueous MFC and NFC suspensions. Morphological and structural properties of the dried micro- and nanofibrillated cellulose were examined by scanning electron microscopy (FE-SEM) and Fourier transform infrared spectroscopy (FT-IR). FE-SEM revealed dense textured translucent film of randomly arranged fibrils in air dried samples, while freeze drying of MFC and NFC suspension resulted in formation of irregularly shaped agglomerates with dimensions up to 80 μm. The drying process of MFC and NFC, however, did not lead to a change in chemical structure since the FTIR spectra were identical.
Sekundarne ključne besede:	cellulose;MFC;NFC;air drying;freeze drying;microscopy;spectroscopy;