Proučevali smo varjenje TIG in lasersko varjenje orodnih jekel 1.2379 ter 1.2343 in ju primerjali s stališča velikosti ter trdote vara. Navarili smo tri vzorce z varjenjem TIG ter deset vzorcev z laserskim varjenjem. Uporabljeni so bili različni parametri in pogoji za posamezen vzorec. Izmerili smo trdote varov posameznih vzorcev po Vickersu, pri čemer je bila pri laserskem varjenju obtežba 200 g, pri TIG varjenju pa 300 g. Proučili ter primerjali smo izmerjene trdote. Ugotovili smo, da je izmerjena trdota pri TIG vzorcih v navaru nižja od izmerjene trdote v TVC, medtem ko je pri laserskih vzorcih trdota najvišja v samem navaru. Na izmerjene vrednosti trdot vplivata tehnologija varjenja in kemična sestava navara, ki je odvisna tudi od uporabljenega dodajnega materiala in zaradi stopnje razmešanja tudi od osnovnega materiala.
Keywords
diplomske naloge;navar;varjenje TIG;lasersko varjenje;navarjanje;trdota;Vickers;
Data
Language: |
Slovenian |
Year of publishing: |
2019 |
Typology: |
2.11 - Undergraduate Thesis |
Organization: |
UL FS - Faculty of Mechanical Engineering |
Publisher: |
[L. Leskovec] |
UDC: |
621.791.7(043.2) |
COBISS: |
16897307
|
Views: |
775 |
Downloads: |
253 |
Average score: |
0 (0 votes) |
Metadata: |
|
Other data
Secondary language: |
English |
Secondary title: |
Comparison of laser and TIG welding |
Secondary abstract: |
We studied TIG and laser welding of tool steel 1.2379 and 1.2343 and made a comparison between them. We used TIG welding for 3 samples and laser welding for 10 samples. For each sample we used different welding parameters and conditions. We measured Vickers hardness of welds and heat affected zone for each sample. At laser welding we applied force of 200 g, and at TIG welding a force of 300 g. We studied and compared measured results. We came to the conclusion that the measured hardness of TIG welding samples was lower inside the weld compared to the measured hardness in heat affected zone. At laser welding samples we concluded the opposite % measured hardness was the highest inside the weld, due to higher temperature gradients. Chemical composition of the weld, which is influenced by welding technology and composition of welding material and to some degree also by composition of base metal (because of metal mixing), has the biggest impact on obtained results. |
Secondary keywords: |
weld;TIG welding;laser welding;cladding;hardness;Vickers; |
Type (COBISS): |
Final paper |
Study programme: |
0 |
Embargo end date (OpenAIRE): |
1970-01-01 |
Thesis comment: |
Univ. v Ljubljani, Fak. za strojništvo |
Pages: |
XVI, 56 f. |
ID: |
11230333 |