zaključna naloga Razvojno raziskovalnega programa I. stopnje Strojništvo
Luka Leskovec (Avtor), Damjan Klobčar (Mentor)

Povzetek

Proučevali smo varjenje TIG in lasersko varjenje orodnih jekel 1.2379 ter 1.2343 in ju primerjali s stališča velikosti ter trdote vara. Navarili smo tri vzorce z varjenjem TIG ter deset vzorcev z laserskim varjenjem. Uporabljeni so bili različni parametri in pogoji za posamezen vzorec. Izmerili smo trdote varov posameznih vzorcev po Vickersu, pri čemer je bila pri laserskem varjenju obtežba 200 g, pri TIG varjenju pa 300 g. Proučili ter primerjali smo izmerjene trdote. Ugotovili smo, da je izmerjena trdota pri TIG vzorcih v navaru nižja od izmerjene trdote v TVC, medtem ko je pri laserskih vzorcih trdota najvišja v samem navaru. Na izmerjene vrednosti trdot vplivata tehnologija varjenja in kemična sestava navara, ki je odvisna tudi od uporabljenega dodajnega materiala in zaradi stopnje razmešanja tudi od osnovnega materiala.

Ključne besede

diplomske naloge;navar;varjenje TIG;lasersko varjenje;navarjanje;trdota;Vickers;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FS - Fakulteta za strojništvo
Založnik: [L. Leskovec]
UDK: 621.791.7(043.2)
COBISS: 16897307 Povezava se bo odprla v novem oknu
Št. ogledov: 775
Št. prenosov: 253
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Comparison of laser and TIG welding
Sekundarni povzetek: We studied TIG and laser welding of tool steel 1.2379 and 1.2343 and made a comparison between them. We used TIG welding for 3 samples and laser welding for 10 samples. For each sample we used different welding parameters and conditions. We measured Vickers hardness of welds and heat affected zone for each sample. At laser welding we applied force of 200 g, and at TIG welding a force of 300 g. We studied and compared measured results. We came to the conclusion that the measured hardness of TIG welding samples was lower inside the weld compared to the measured hardness in heat affected zone. At laser welding samples we concluded the opposite % measured hardness was the highest inside the weld, due to higher temperature gradients. Chemical composition of the weld, which is influenced by welding technology and composition of welding material and to some degree also by composition of base metal (because of metal mixing), has the biggest impact on obtained results.
Sekundarne ključne besede: weld;TIG welding;laser welding;cladding;hardness;Vickers;
Vrsta dela (COBISS): Zaključna naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Fak. za strojništvo
Strani: XVI, 56 f.
ID: 11230333
Priporočena dela:
, zaključna naloga Razvojno raziskovalnega programa I. stopnje Strojništvo
, zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program
, critical raw material perspective
, zaključna naloga Razvojno raziskovalnega programa I. stopnje Strojništvo
, diplomsko delo