Vladimir Gliha (Author), Tomaž Vuherer (Author)

Abstract

The effects of small, artificial surface defects on the fatigue strength of coarse grain HAZ material found at the weld toe were studied. The size of defects did not exceed the grain size, which is the most relevant microstructural unit of polycrystalline metals. The artificial defects were made by indenting the material with Vicker`s pyramid and by drilling holes. The samples of coarse-grain HAZ material were prepared using a welding thermal-cycle simulator or furnace. The mexperimentally determined bending fatigue strength versus the properly evaluated defects siye was compared with the propagation of long cracks. Residual stresses appear when making small artificial defects. The crack initiation from the defects was analysed and theinfluence of residual stresses is discussed.

Keywords

varjenje;zvarni spoji;TVP;rob zvara;groba zrna;dinamična trdnost;umetne napake;stabilna razpoka;zaostale napetosti;welding;welded joints;HAZ;weld toe;coarse grain;fatigue strength;artificial defect;residual stresses;non-propagating crack;

Data

Language: English
Year of publishing:
Typology: 1.01 - Original Scientific Article
Organization: UM FS - Faculty of Mechanical Engineering
Publisher: Inštitut za kovinske materiale in tehnologije Ljubljana
UDC: 621.791.05:620.178.152.3
COBISS: 11446550 Link will open in a new window
ISSN: 1580-2949
Parent publication: Materiali in tehnologije
Views: 1148
Downloads: 85
Average score: 0 (0 votes)
Metadata: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Other data

Secondary language: Slovenian
Secondary title: Vedenje jekla grobozrnatega TVP z napakami pri ciklični obremenitvi
Secondary abstract: Raziskan je bil vpliv majhnih umetnih napak na dinamično trdnost grobozrnatega dela TVP ob robu zvarov. Napake niso bile večje od kristalnih zrn, ki so najbolj pomembna enota polikristalnih materialov. Umetne napake smo ustvarili z odtiskovanjem Vickesove piramide in vrtanjem. Preizkušance z grobozrnatim jeklom TVP smo pripravili v simulatorju termičnega cikla in v peči. Eksperimentalno določeno upogibno dinamično trdnost v odvisnosti od velikosti napake smo primerjali s propagacijo dolgih razpok. S pripravo umetnih napak nastanejo zaostale napetosti. V razpravi je govor o začetku razpoke iz napak in o vplivu zaostalih napetosti.
Secondary keywords: welding;welded joints;HAZ;weld toe;coarse grain;fatigue strength;artificial defect;residual stresses;non-propagating crack;
URN: URN:NBN:SI
Type (COBISS): Scientific work
Pages: str. 125-130
Volume: ǂLetn. ǂ41
Issue: ǂšt. ǂ3
Chronology: 2007
ID: 1738849