Vladimir Gliha (Avtor), Tomaž Vuherer (Avtor)

Povzetek

The effects of small, artificial surface defects on the fatigue strength of coarse grain HAZ material found at the weld toe were studied. The size of defects did not exceed the grain size, which is the most relevant microstructural unit of polycrystalline metals. The artificial defects were made by indenting the material with Vicker`s pyramid and by drilling holes. The samples of coarse-grain HAZ material were prepared using a welding thermal-cycle simulator or furnace. The mexperimentally determined bending fatigue strength versus the properly evaluated defects siye was compared with the propagation of long cracks. Residual stresses appear when making small artificial defects. The crack initiation from the defects was analysed and theinfluence of residual stresses is discussed.

Ključne besede

varjenje;zvarni spoji;TVP;rob zvara;groba zrna;dinamična trdnost;umetne napake;stabilna razpoka;zaostale napetosti;welding;welded joints;HAZ;weld toe;coarse grain;fatigue strength;artificial defect;residual stresses;non-propagating crack;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UM FS - Fakulteta za strojništvo
Založnik: Inštitut za kovinske materiale in tehnologije Ljubljana
UDK: 621.791.05:620.178.152.3
COBISS: 11446550 Povezava se bo odprla v novem oknu
ISSN: 1580-2949
Matična publikacija: Materiali in tehnologije
Št. ogledov: 1148
Št. prenosov: 85
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarni naslov: Vedenje jekla grobozrnatega TVP z napakami pri ciklični obremenitvi
Sekundarni povzetek: Raziskan je bil vpliv majhnih umetnih napak na dinamično trdnost grobozrnatega dela TVP ob robu zvarov. Napake niso bile večje od kristalnih zrn, ki so najbolj pomembna enota polikristalnih materialov. Umetne napake smo ustvarili z odtiskovanjem Vickesove piramide in vrtanjem. Preizkušance z grobozrnatim jeklom TVP smo pripravili v simulatorju termičnega cikla in v peči. Eksperimentalno določeno upogibno dinamično trdnost v odvisnosti od velikosti napake smo primerjali s propagacijo dolgih razpok. S pripravo umetnih napak nastanejo zaostale napetosti. V razpravi je govor o začetku razpoke iz napak in o vplivu zaostalih napetosti.
Sekundarne ključne besede: welding;welded joints;HAZ;weld toe;coarse grain;fatigue strength;artificial defect;residual stresses;non-propagating crack;