magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
Nejc Avbelj (Author), Uroš Trdan (Mentor), Damjan Klobčar (Co-mentor)

Abstract

Vedno večje je povpraševanje po lahkih materialih z dobrimi mehanskimi lastnostmi. Temu se ustrezno hitro razvijajo tudi izdelovalne tehnologije, s katerimi poskušamo doseči čim boljšo kvaliteto s čim nižjimi stroški izdelave. V porastu so aditivne tehnologije, ki nudijo številne poenostavitve pri izdelavi izdelkov s kompleksno geometrijo. Postopek oblikovnega obločnega navarjanja - WAAM ima kljub prednostim tudi določene slabosti. Težave se pojavijo pri kontroli ohlajanja taline, večji poroznosti in anizotropiji mikrostrukture, kar vodi v slabše mehanske lastnosti izdelka. Napreden način izdelave kovinskih izdelkov predstavlja CMT proces varjenja med katerim na izdelek sočasno prenašamo vibracije. Te učinkovito vplivajo na mehanizme formiranja mikrostrukture, pospešijo razplinjanje taline in zmanjšajo anizotropijo materiala. Posledi čno lahko dobimo var z bolj homogeno mikrostrukturo, 200 % manjšo poroznostjo in boljšimi mehanskimi lastnostmi.

Keywords

magistrske naloge;aluminijeva zlitina - AlMg5;oblikovno obločno navarjanje - WAAM;hladen prenos kovine - CMT;vibracije;mikrostruktura;poroznost;zaostale napetosti;natezna trdnost;

Data

Language: Slovenian
Year of publishing:
Typology: 2.09 - Master's Thesis
Organization: UL FS - Faculty of Mechanical Engineering
Publisher: [N. Avbelj]
UDC: 621.791:621.9.04:539.412(043.2)
COBISS: 219830787 Link will open in a new window
Views: 172
Downloads: 47
Average score: 0 (0 votes)
Metadata: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Other data

Secondary language: English
Secondary title: Effect of vibrations on microstructural anisotropy and mechanical properties of wire arc additive manufactured aluminium alloy
Secondary abstract: The demand for lightweight materials with good mechanical properties is increasing. Accordingly, manufacturing technologies are also rapidly developing, aiming to achieve the best possible quality at the lowest possible production costs. Additive technologies, which offer numerous simplifications in the production of complex geometric products, are on the rise. The WAAM process, despite its advantages, also has certain weaknesses. Issues include the control of melt cooling, higher porosity, anisotropy of the microstructure, and consequently poorer mechanical properties of the product. An advanced method of manufacturing metal products is represented by the CMT process, during which vibrations are simultaneously applied to the product. These effectively influence the mechanisms of microstructure formation, accelerate the degassing of the melt, and reduce material anisotropy. Consequently, we can obtain a weld with more homogeneous microstructure, 200 % less porosity, and better mechanical properties.
Secondary keywords: master thesis;aluminium alloy - AlMg5;wire arc additiv manufacturing - WAAM;cold metal transfer - CMT;vibrations;microstructure;porosity;residual stress;tensile strength;
Type (COBISS): Master's thesis/paper
Study programme: 0
Embargo end date (OpenAIRE): 1970-01-01
Thesis comment: Univ. Ljubljana, Fak. za strojništvo
Pages: XXIV, 79 str.
ID: 25031361
Recommended works:
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo - Projektno aplikativni program
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo - Projektno aplikativni program
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo