Nejc Avbelj (Avtor), Uroš Trdan (Mentor), Damjan Klobčar (Komentor)

Povzetek

Vedno večje je povpraševanje po lahkih materialih z dobrimi mehanskimi lastnostmi. Temu se ustrezno hitro razvijajo tudi izdelovalne tehnologije, s katerimi poskušamo doseči čim boljšo kvaliteto s čim nižjimi stroški izdelave. V porastu so aditivne tehnologije, ki nudijo številne poenostavitve pri izdelavi izdelkov s kompleksno geometrijo. Postopek oblikovnega obločnega navarjanja - WAAM ima kljub prednostim tudi določene slabosti. Težave se pojavijo pri kontroli ohlajanja taline, večji poroznosti in anizotropiji mikrostrukture, kar vodi v slabše mehanske lastnosti izdelka. Napreden način izdelave kovinskih izdelkov predstavlja CMT proces varjenja med katerim na izdelek sočasno prenašamo vibracije. Te učinkovito vplivajo na mehanizme formiranja mikrostrukture, pospešijo razplinjanje taline in zmanjšajo anizotropijo materiala. Posledi čno lahko dobimo var z bolj homogeno mikrostrukturo, 200 % manjšo poroznostjo in boljšimi mehanskimi lastnostmi.

Ključne besede

magistrske naloge;aluminijeva zlitina - AlMg5;oblikovno obločno navarjanje - WAAM;hladen prenos kovine - CMT;vibracije;mikrostruktura;poroznost;zaostale napetosti;natezna trdnost;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.09 - Magistrsko delo
Organizacija: UL FS - Fakulteta za strojništvo
Založnik: [N. Avbelj]
UDK: 621.791:621.9.04:539.412(043.2)
COBISS: 219830787 Povezava se bo odprla v novem oknu
Št. ogledov: 172
Št. prenosov: 47
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Effect of vibrations on microstructural anisotropy and mechanical properties of wire arc additive manufactured aluminium alloy
Sekundarni povzetek: The demand for lightweight materials with good mechanical properties is increasing. Accordingly, manufacturing technologies are also rapidly developing, aiming to achieve the best possible quality at the lowest possible production costs. Additive technologies, which offer numerous simplifications in the production of complex geometric products, are on the rise. The WAAM process, despite its advantages, also has certain weaknesses. Issues include the control of melt cooling, higher porosity, anisotropy of the microstructure, and consequently poorer mechanical properties of the product. An advanced method of manufacturing metal products is represented by the CMT process, during which vibrations are simultaneously applied to the product. These effectively influence the mechanisms of microstructure formation, accelerate the degassing of the melt, and reduce material anisotropy. Consequently, we can obtain a weld with more homogeneous microstructure, 200 % less porosity, and better mechanical properties.
Sekundarne ključne besede: master thesis;aluminium alloy - AlMg5;wire arc additiv manufacturing - WAAM;cold metal transfer - CMT;vibrations;microstructure;porosity;residual stress;tensile strength;
Vrsta dela (COBISS): Magistrsko delo/naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. Ljubljana, Fak. za strojništvo
Strani: XXIV, 79 str.
ID: 25031361
Priporočena dela:
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo - Projektno aplikativni program
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo - Projektno aplikativni program
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo