diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo - Projektno aplikativni program
Blaž Malavašič (Author), Sebastjan Žagar (Mentor), Roman Šturm (Co-mentor)

Abstract

Aluminijeve zlitine serije 7xxx zaradi svoje nizke mase in visoke trdnosti predstavljajo veliko vlogo v letalski in transportni industriji. V tem delu je obravnavana aluminijeva zlitina 7075, katere mehanske lastnosti smo dodatno izboljšali z izločevalnim utrjevanjem. Staranje smo izvedli pri treh različnih temperaturah (105 ▫$^°$▫C, 120 ▫$^°$▫C in 140 ▫$^°$▫C) ter različnih časih. Rezultate toplotne obdelave smo analizirali na podlagi spremembe trdote, električne prevodnosti in korozijske odpornosti. Izločene faze v mikrostrukturi smo na koncu ovrednotili še z metalografsko analizo s pomočjo svetlobnega optičnega mikroskopa.

Keywords

diplomske naloge;aluminijeva zlitina 7075;izločevalno utrjevanje;trdota;korozija aluminija;električna prevodnost;mikrostruktura;

Data

Language: Slovenian
Year of publishing:
Typology: 2.11 - Undergraduate Thesis
Organization: UL FS - Faculty of Mechanical Engineering
Publisher: [B. Malavašič]
UDC: 621.785.7:669.715:620.18(043.2)
COBISS: 248439043 Link will open in a new window
Views: 62
Downloads: 4
Average score: 0 (0 votes)
Metadata: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Other data

Secondary language: English
Secondary title: Precipitation hardening of aluminum alloy 7075
Secondary abstract: Aluminium alloys of the 7xxx series, due to their low density and high strength, play a significant role in the aerospace and transportation industries. This study focuses on the aluminium alloy 7075, whose mechanical properties were further enhanced through precipitation hardening. Ageing was conducted at three different temperatures (105 ▫$^°$▫C, 120 ▫$^°$▫C and 140▫$^°$▫C) and for various durations. The effects of the heat treatment were evaluated based on changes in hardness, electrical conductivity and corrosion resistance. Finally, the precipitated phases in the microstructure were characterised through metallographic examination using an optical light microscope.
Secondary keywords: thesis;aluminum alloy 7075;precipitation hardening;hardness;aluminum corrosion;electrical conductivity;microstructure;
Type (COBISS): Bachelor thesis/paper
Study programme: 0
Thesis comment: Univ. v Ljubljani, Fak. za strojništvo
Pages: XX, 48 str.
ID: 27349196
Recommended works:
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo - Projektno aplikativni program
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo
, zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program
, diplomsko delo
, diplomsko delo