zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program
Urška Čavič (Avtor), Roman Šturm (Mentor)

Povzetek

V zaključni nalogi smo različno starane kose aluminijeve zlitine 7075 kavitacijsko utrdili in določili njihove mehanske lastnosti. Zanimal nas je vpliv kavitacijskega utrjevanja na hrapavost površine, električno prevodnost, mikrotrdoto in mikrostrukturo predhodno starane aluminijeve zlitine. Aluminijevo zlitino smo najprej starali pri 145°C, 170°C ali 195°C, eden izmed vzorcev pa ni bil staran. Vsi vzorci so bili nato kavitacijsko utrjeni z 40% pokritostjo. Ugotovili smo da po kavitacijskem utrjevanju površini povišamo hrapavost in povišamo trdoto v primeru da zlitina ni predhodno prestarana. Bolj kot je vzorec prestaran višjo hrapavost površine dobimo po utrjevanju, samo povišanje trdote pa ne pride tolik do izraza, v skrajnem primeru lahko material celo omehčamo.

Ključne besede

diplomske naloge;kavitacijsko utrjevanje;aluminijeve zlitine;Al 7075;staranje;mehanske lastnosti;mikrotrdota;hrapavost površine;električna prevodnost;mikrostruktura;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FS - Fakulteta za strojništvo
Založnik: [U. Čavič]
UDK: 621.789:532.528:669.715(043.2)
COBISS: 78740739 Povezava se bo odprla v novem oknu
Št. ogledov: 618
Št. prenosov: 53
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Determination of mechanical properties of water peened aluminium alloy Al 7075
Sekundarni povzetek: In this final thesis differently aged specimens of aluminium alloy 7075 were water peened and their mechanical properties were analised. The influence of water peening on surface roughness, electrical conductivity, microhardness and microstructure of aged aluminium alloy was investigated. First the aluminium alloy was aged at 145°C, 170°C or 195°C, besides one specimen that was not aged. All of the specimen were water peened with 40% coverage. Analysis of the results shows that the surface roughness and hardness of material increase after water peening. Overaging of the material results in higher surface rougness and barely any change in hardness. Water peening of the overaged material can even result in decreased hardness of the material.
Sekundarne ključne besede: thesis;water peening;aluminium alloys;Al 7075;ageing;mechanical properties;microhardness;surface roughness;electrical conductivity;microctructure;
Vrsta dela (COBISS): Zaključna naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Fak. za strojništvo
Strani: XIV, 34 f.
ID: 13363320
Priporočena dela:
, zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo
, ni podatka o podnaslovu
, doktorska disertacija
, diplomsko delo