Secondary abstract: | The quasicrystalline phase in melt-spun Al-Mn-Be alloys was investigated. In ribbons 40-60 ▫$/mu$▫m thick the phase was present in the form of small particles rather uniformly dispersed in an aluminium solid solution matrix. The quasicrystalline phase had a primitive icosahedral structure. It was confirmed that it contained a substantial amount of Be. Nonetheless, it seemed that the electron-to-atom ratio remained close to that of binary Al80Mn20 quasicrystal. |
Secondary keywords: | kvazikristali;hitro strjevanje;mikrostruktura;metalografija; |
URN: | URN:SI:UM: |
Type (COBISS): | Not categorized |
Pages: | str. 343-347 |
Volume: | ǂVol. ǂ452 |
Issue: | ǂiss. ǂ2 |
Chronology: | Mar. 2008 |
ID: | 8718558 |