The quasicrystalline phase in melt-spun Al-Mn-Be alloys was investigated. In ribbons 40-60 ▫$/mu$▫m thick the phase was present in the form of small particles rather uniformly dispersed in an aluminium solid solution matrix. The quasicrystalline phase had a primitive icosahedral structure. It was confirmed that it contained a substantial amount of Be. Nonetheless, it seemed that the electron-to-atom ratio remained close to that of binary Al80Mn20 quasicrystal.

Ključne besede

kvazikristali;hitro strjevanje;mikrostruktura;metalografija;quasicrystals;rapid solidification;microstructure;metallography;electron emission spectroscopies;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UL NTF - Naravoslovnotehniška fakulteta
UDK: 669
COBISS: 687199 Povezava se bo odprla v novem oknu
ISSN: 0925-8388
Št. ogledov: 1627
Št. prenosov: 88
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni povzetek: The quasicrystalline phase in melt-spun Al-Mn-Be alloys was investigated. In ribbons 40-60 ▫$/mu$▫m thick the phase was present in the form of small particles rather uniformly dispersed in an aluminium solid solution matrix. The quasicrystalline phase had a primitive icosahedral structure. It was confirmed that it contained a substantial amount of Be. Nonetheless, it seemed that the electron-to-atom ratio remained close to that of binary Al80Mn20 quasicrystal.
Sekundarne ključne besede: kvazikristali;hitro strjevanje;mikrostruktura;metalografija;
URN: URN:SI:UM:
Vrsta dela (COBISS): Delo ni kategorizirano
Strani: str. 343-347
Letnik: ǂVol. ǂ452
Zvezek: ǂiss. ǂ2
Čas izdaje: Mar. 2008
ID: 8718558
Priporočena dela:
, ni podatka o podnaslovu
, ni podatka o podnaslovu