Abstract

A nitrogen laser beam (337 nm, 6 ns (FWHM), (3.2 [plus minus] 0.2) mJ) was focused with a quartz lens (f = 100 mm) onto an aluminium target in air at normal pressure. The laser irradiation and plasma explosion caused a modification to the Al surface and the deposition of a thin film (droplets) onto a glassy carbon plate. The irradiated target and the deposited material were studied with a scanning electron microscope (SEM) and a focused-ion-beam (FIB) device. A crater surrounded by a rim was produced on the spot of maximum irradiation on the aluminium target. The crater, very deep in comparison to its width and thickness, was presumably caused by the Kelvin-Helmholtz and the Rayleigh-Taylor instabilities. The temperatures of the electron and the massive particles were explained.

Keywords

aluminium;laser ablation;thin film deposition;instabilities;temperatures;

Data

Language: English
Year of publishing:
Typology: 1.01 - Original Scientific Article
Organization: UM FS - Faculty of Mechanical Engineering
Publisher: Inštitut za kovinske materiale in tehnologije Ljubljana
UDC: 669.71:620.1/.2
COBISS: 678058 Link will open in a new window
ISSN: 1580-2949
Parent publication: Materiali in tehnologije
Views: 836
Downloads: 86
Average score: 0 (0 votes)
Metadata: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Other data

Secondary language: Slovenian
Secondary title: Obsevanje aluminijaste tarče z laserjem
Secondary abstract: Žarek laserske svetlobe (337 nm, 6 ns ((FWHM), (3.2 [plus minus] 0.2) mJ) smo s kremenovo lečo (f = 100 mm) fokusirali na aluminijevo tarčo, ki je bila na zraku pri normalnem zračnem tlaku. Obsevanje z laserjem in eksplozija plazme sta povzročila spremembo površine aluminija ter nanos tanke plasti in kapljic na steklasto ogljikovo ploščico. Obsevano tarčo in nanesen material smo raziskali z vrstičnim elektronskim mikroskopom (SEM) in s fokusiranim ionskim curkom (FIB). Na aluminijevi tarči je na najbolj obsevanem mestu nastal krater, ki je bil zelo globok v primerjavi z njegovo širino in debelino. Krater je bil povzročen zaradi Kelvin-Helmholtzove in Rayleigh-Taylorjeve nestabilnosti. V delu smo razložili tudi temperaturo elektronov in temperaturo masivnih delcev.
Secondary keywords: aluminij;laserska ablacija;nanašanje tanke plasti;nestabilnosti;temperatura;
URN: URN:NBN:SI
Type (COBISS): Scientific work
Pages: str. 111-115
Volume: ǂVol. ǂ42
Issue: ǂno. ǂ3
Chronology: 2008
ID: 9593831
Recommended works:
, no subtitle data available
, zaključna naloga Razvojno raziskovalnega programa I. stopnje Strojništvo