Povzetek

A nitrogen laser beam (337 nm, 6 ns (FWHM), (3.2 [plus minus] 0.2) mJ) was focused with a quartz lens (f = 100 mm) onto an aluminium target in air at normal pressure. The laser irradiation and plasma explosion caused a modification to the Al surface and the deposition of a thin film (droplets) onto a glassy carbon plate. The irradiated target and the deposited material were studied with a scanning electron microscope (SEM) and a focused-ion-beam (FIB) device. A crater surrounded by a rim was produced on the spot of maximum irradiation on the aluminium target. The crater, very deep in comparison to its width and thickness, was presumably caused by the Kelvin-Helmholtz and the Rayleigh-Taylor instabilities. The temperatures of the electron and the massive particles were explained.

Ključne besede

aluminium;laser ablation;thin film deposition;instabilities;temperatures;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UM FS - Fakulteta za strojništvo
Založnik: Inštitut za kovinske materiale in tehnologije Ljubljana
UDK: 669.71:620.1/.2
COBISS: 678058 Povezava se bo odprla v novem oknu
ISSN: 1580-2949
Matična publikacija: Materiali in tehnologije
Št. ogledov: 836
Št. prenosov: 86
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarni naslov: Obsevanje aluminijaste tarče z laserjem
Sekundarni povzetek: Žarek laserske svetlobe (337 nm, 6 ns ((FWHM), (3.2 [plus minus] 0.2) mJ) smo s kremenovo lečo (f = 100 mm) fokusirali na aluminijevo tarčo, ki je bila na zraku pri normalnem zračnem tlaku. Obsevanje z laserjem in eksplozija plazme sta povzročila spremembo površine aluminija ter nanos tanke plasti in kapljic na steklasto ogljikovo ploščico. Obsevano tarčo in nanesen material smo raziskali z vrstičnim elektronskim mikroskopom (SEM) in s fokusiranim ionskim curkom (FIB). Na aluminijevi tarči je na najbolj obsevanem mestu nastal krater, ki je bil zelo globok v primerjavi z njegovo širino in debelino. Krater je bil povzročen zaradi Kelvin-Helmholtzove in Rayleigh-Taylorjeve nestabilnosti. V delu smo razložili tudi temperaturo elektronov in temperaturo masivnih delcev.
Sekundarne ključne besede: aluminij;laserska ablacija;nanašanje tanke plasti;nestabilnosti;temperatura;
URN: URN:NBN:SI
Vrsta dela (COBISS): Znanstveno delo
Strani: str. 111-115
Letnik: ǂVol. ǂ42
Zvezek: ǂno. ǂ3
Čas izdaje: 2008
ID: 9593831
Priporočena dela:
, ni podatka o podnaslovu
, zaključna naloga Razvojno raziskovalnega programa I. stopnje Strojništvo