zaključna naloga Razvojno raziskovalnega programa I. stopnje Strojništvo
Jan Janežič (Avtor), Lidija Slemenik Perše (Mentor)

Povzetek

Namen zaključne naloge je raziskava in določitev vpliva temperature tiskanja na mehanske in geometrijske lastnosti 3D tiskanih izdelkov. V okviru naloge smo s pomočjo namiznega 3D tiskalnika Sharebot natisnili vzorce za natezni preizkus standardnih dimenzij po ISO 527. Vzorce smo natisnili s pomočjo filamentov polilaktične kisline (PLA) pri različnih temperaturah šobe na tiskalni glavi, vsi ostali parametri tiskanja so bili ves čas enaki. Temperaturo šobe smo spreminjali v inkrementih po 10°C v območju od 170°C do 230°C. Vpliv temperature na geometrijske lastnosti smo določili z merjenjem geometrije na izbranih mestih, mehanske lastnosti preizkušancev pa smo določili s pomočjo nateznega preizkusa in nanoindentacije. Na podlagi meritev smo želeli določiti optimalno temperaturno območje tiskanja, pri katerem bi 3D tiskani izdelki imeli najboljše mehanske in geometrijske lastnosti. Rezultati meritev so pokazali, da so bili vzorci geometrijsko najbolj stabilni in so imeli najboljše mehanske lastnosti pri tiskanju s temperaturo 200 °C.

Ključne besede

diplomske naloge;3D tiskanje;temperatura;dimenzijska stabilnost;mehanske lastnosti;natezni preizkusi;nanoindentacija;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FS - Fakulteta za strojništvo
Založnik: [J. Janežič]
UDK: 621.9.04:536.5:620.17(043.2)
COBISS: 17092123 Povezava se bo odprla v novem oknu
Št. ogledov: 1523
Št. prenosov: 217
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: The influence of temperature on mechanical properties of 3D printed products
Sekundarni povzetek: The purpose of the presented thesis is to investigate the effect of printing temperature on the mechanical and geometric properties of 3D printed polymer products. As part of the study, samples for tensile testing of standard dimensions according to ISO 527 were printed using the Sharebot desktop 3D printer. Samples were printed with polylactid filaments (PLA) at different temperatures of the nozzle on the printhead, while all other printing parameters were kept constant. The nozzle temperature was changed in increments of 10 °C in the range from 170 °C to 230 °C. The influence of printing temperature on the geometric properties was determined by measuring the geometry at selected points, while the mechanical properties of the tested products were determined by tensile test and nanoindentation. On the basis of measurements, we tried to determine the optimal printing temperature range in which 3D printed products would have the best mechanical and geometric properties. The results showed that the samples were geometrically the most stable and had the best mechanical properties at printing temperature of 200 °C.
Sekundarne ključne besede: 3D printing;temperature;dimensional stability;mechanical properties;tensile tests;nanoindentation;
Vrsta dela (COBISS): Zaključna naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Fak. za strojništvo
Strani: XV, 42 f., [7] f. pril.
ID: 11439346
Priporočena dela:
, zaključna naloga Razvojno raziskovalnega programa I. stopnje Strojništvo
, ni podatka o podnaslovu
, ni podatka o podnaslovu
, zaključna naloga Razvojno raziskovalnega programa I. stopnje Strojništvo
, zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program