zaključna naloga Razvojno raziskovalnega programa I. stopnje Strojništvo
Žan Kavčič (Avtor), Joško Valentinčič (Mentor), Roman Šturm (Komentor)

Povzetek

3D-tisk je proces izdelave izdelka, plast za plastjo. Obsega različne tehnologije. V zaključni nalogi smo se osredotočili na metodo ciljnega nalaganja. Zanimalo nas je, kako stopnja notranje zapolnitve vpliva na mehanske lastnosti izdelka iz materiala PLA. Po standardih za polimerne materiale smo natisnili preizkušance ter nato naredili test na napravah za upogibni in udarni preizkus. Udarno žilavost smo izračunali iz razmerja udarnega dela in površine preseka vzorca na mestu preloma. Pri upogibnem preizkusu smo merili silo in izračunali upogibno napetost. Ugotovitve so bile, da je material PLA krhek. Mehanske lastnosti se višajo z večanjem stopnje zapolnjenosti. Pri manj obremenjenih delih bi zato uporabili minimalne stopnje zapolnitev, medtem ko bi za bolj obremenjene predele uporabili najvišjo stopnjo zapolnitve.

Ključne besede

diplomske naloge;mehanske lastnosti;3D-tiskanje;metoda ciljnega nalaganja;stopnja notranje zapolnitve;udarni preizkus;upogibni preizkus;aditivne tehnologije;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FS - Fakulteta za strojništvo
Založnik: [Ž. Kavčič]
UDK: 621.9.04:678:620.17(043.2)
COBISS: 16868123 Povezava se bo odprla v novem oknu
Št. ogledov: 1192
Št. prenosov: 251
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Mechanical properties of 3D printed part from PLA material
Sekundarni povzetek: 3D printing is the process of making a product, layer by layer. It encompasses various technologies. In the final thesis, we focused on the fused deposition modelling. We were interested in how the degree of internal filling affects the mechanical properties of a PLA material. According to the standards for polymeric materials, we printed out the test pieces and then tested them on the devices for bending and impact testing. Impact toughness was calculated from the ratio of the impact part and the cross-sectional area of the specimen at the fracture site. In the bending test the force was measured and the bending tension was calculated. The findings were that PLA material is fragile. The mechanical properties increase as the occupancy rate increases. For less congested parts, therefore, minimum fill rates would be used, while for more congested areas the highest fill rate would be used.
Sekundarne ključne besede: mechanical properties;3D-printing;fused deposition modelling;degree of internal filling;impact test;bending test;additive technologies;
Vrsta dela (COBISS): Zaključna naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Fak. za strojništvo
Strani: XIV, 31 f.
ID: 11235618
Priporočena dela:
, zaključna naloga Razvojno raziskovalnega programa I. stopnje Strojništvo
, zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo