Metal-ceramic fusing has been the essential step in obtaining materials that benefit from both ceramic and metal constituents, i.e. where the combined properties of metal and ceramic layers are desirable. When considering fusing methods, soldering and active metal brazing are the most effective. These processes involve braze melting and flowing between the two pieces of material. In the first part the phenomena occurring on the boundary between the ceramics and the active filler metal during the metal-ceramics joining are discussed. Three interconnected sub-processes are considered: (1) wetting of the ceramic surface, (2) chemical reactions at the interface and (3) diffusion with a moving interface. Then, the appearances at the grain boundary grooves of the ceramic surface are presented as phenomena on the catalytic surface. In the second part, examples from dental practice and jewellery manufacturing are used for comparative analysis. Finally, we discuss the composition and properties of the soldering and brazing alloys used for dental practice and jewellery manufacturing.

Ključne besede

metal-ceramic bonding;brazing;soldering;dentistry;jewellery;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.02 - Pregledni znanstveni članek
Organizacija: UM FS - Fakulteta za strojništvo
Založnik: Inštitut za kovinske materiale in tehnologije Ljubljana
UDK: 669:666:616.31:739
COBISS: 14027542 Povezava se bo odprla v novem oknu
ISSN: 1580-2949
Matična publikacija: Materiali in tehnologije
Št. ogledov: 960
Št. prenosov: 79
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarni naslov: Staljene vmesne površine med kovino in keramiko v zobozdravstvu in pri izdelavi nakita
Sekundarni povzetek: Zlitje kovine in keramike je temeljna stopnja za nastanek materiala, ki pridobi lastnosti obeh sestavnih delov, kjer je želena kombinacija lastnosti plasti kovine in keramike. Od metod zlitja sta lotanje in aktivno spajkanje najbolj učinkoviti. Procese sestavljata taljenje in pretok taline med obema materialoma. V prvem delu razpravljamo o procesih na meji med keramiko in aktivnim polnilnim materialom med spajanjem kovine in keramike. Obravnavamo tri povezane procese: (1) omo~ljivost keramične površine, (2) kemične reakcije na vmesni površini in (3) difuzijo s premikajočo se mejno površino. Nato obravnavamo nastanek žlebov na mejah zrn na katalitični površini. V drugem delu uporabljamo primere iz dentalne prakse in izdelave nakita za primerjalno analizo. Na koncu je razprava o sestavi in lastnostih spajk in lotov, ki se uporabljajo v dentalni praksi in pri izdelavi nakita.
Sekundarne ključne besede: vezava keramika-kovina;lotanje;spajkanje;zobozdravstvo;nakit;
URN: URN:NBN:SI
Vrsta dela (COBISS): Znanstveno delo
Strani: str. 59-66
Letnik: ǂLetn. ǂ44
Zvezek: ǂšt. ǂ2
Čas izdaje: 2010
ID: 1731247