Karlo Raić (Avtor), Rebeka Rudolf (Avtor), Borut Kosec (Avtor), Ivan Anžel (Avtor), Vojkan Lazić (Avtor), Aleksandar Todorović (Avtor)

Povzetek

This paper describes the development of novel, reactive Al-Au nano-multilayered foils, their possible application in different fields and a discussion of the nano-foils' suitability for dental and jewellery applications. Moreover, this study includes the rapid joining of similar and dissimilar materials, by placing multilayer nano-foils and two layers of solder or braze. The foils precisely control the instantaneous release of heatenergy for the joining and act as a controllable local heat source. The reactive foils' thickness is in the range 10 nm to less than 100 nm and they contain many nanoscale layers that alternate between materials with high mixing heats, such as Al and Au. The foil between the two solder/braze layers melts the solder/braze with the heat generated by the reaction and bonds the components. The use of reactive foils eliminates the need for a furnace and dramatically increases the soldering/brazing heating rate of the components being bonded. Thus, ceramics and metals can be fused over required areas without the thermal stresses that are encountered in furnace soldering or brazing. In addition, a completely new plasma technology is proposed for the manufacturing of nano-foils and the first results of the preliminary experimental testing are presented.

Ključne besede

ceramic-metal bonding;low-temperature;nano-foils;plasma technology;dentistry;jewellery;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UM FS - Fakulteta za strojništvo
Založnik: Inštitut za kovinske materiale in tehnologije
UDK: 669.71'21:621.791.3:616.314-089.28:671.12
COBISS: 13021718 Povezava se bo odprla v novem oknu
ISSN: 1580-2949
Matična publikacija: Materiali in tehnologije
Št. ogledov: 1675
Št. prenosov: 79
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarni naslov: Nanofolije za lotanje pri zobozdravniškem delu in izdelavi nakita
Sekundarni povzetek: Članek opisuje razvoj nanoplastnih reaktivnih Al-Au-folij, njihovo uporabo na različnih področjih in razprava o uporabi v zobni tehniki in pri izdelavi nakita. Študija vključuje hitro spajanje podobnih in različnih materialov s postavitvijo večplastnih nanofolij ter plasti lota med oba dela za spajanje. Folije kontrolirajo hipno sprostitev toplotne energije za spajanje in delujejo kot lokalni vir toplote. Reaktivne folije z debelino od 10 nm do 100 nm so izmenoma iz materialov, ki imajo veliko toploto mešanja, npr. Al in Au. Folija z reakcijsko toploto raztali obe plasti lota in spoji obe lotani komponenti. Pri uporabi reaktivnih folij je peč nepotrebna, zato se zelo poveča hitrost spajanja lotanih komponent. Keramiko in kovine je mogoče spajati na določenih površinah brez toplotnih napetosti, ki nastanejo pri lotanju s segrevanjem v peči. Sugerirana je tudi nova plazemska tehnologija zaizdelavo nanofolij in predstavljeni so prvi rezultati praktičnih preizkusov.
Sekundarne ključne besede: spajanje keramika-kovina;nizke temperature;nanofolije;plazemska tehnologija;zobotehnika;nakit;
URN: URN:NBN:SI
Vrsta dela (COBISS): Znanstveno delo
Strani: str. 3-9
Letnik: ǂLetn. ǂ43
Zvezek: ǂšt. ǂ1
Čas izdaje: 2009
ID: 1733115