Povzetek
Novejše raziskave so pokazale, da lahko z modifikacijo polimerne matrike s polnilom in elastomerno fazo znatno vplivamo na mehanske lastnosti nastalega kompozita. V raziskavah smo uporabili izotaktični PP ter ga modificirali z neobdelanim oz. obdelanim talkom in SEBS oz. SEBS-gMA. Vzorce smo pripravili preko taline v Brabenderjevem gnetilniku in s stiskanjem v plošče na laboratorijski stiskalnici. Karakterizirali smo jih z merjenjem mehanskih lastnosti (Youngov modul, meja plastičnosti, zarezna udarna žilavost) in z opredelitvijo morfologije. Preučevali smo binarne sisteme PP/talk in PP/elastomer z vsebnostjo talka do 16 vol.% in do 10 vol.% elastomera, kakor tudi ternarne kompozite PP/talk/elastomer z 12 vol.% talka. Mejo plastičnosti ternarnih kompozitov smo določili še s polempiričnimi enačbami. Ugotovili smo, da uporaba obdelanih modifikatorjev (talka oz. elastomera) izboljša adhezijo z matriko, kar odseva na mehanskih lastnostih kot boljši prenos napetosti.
Ključne besede
organska kemija;polimeri;termoplasti;kompoziti;karakterizacija;kemija;plastične mase;elastomeri;morfologija;mehanske lastnosti;
Podatki
Jezik: |
Angleški jezik |
Leto izida: |
1999 |
Tipologija: |
1.01 - Izvirni znanstveni članek |
Organizacija: |
UM EPF - Ekonomsko-poslovna fakulteta |
Založnik: |
Slovensko kemijsko društvo |
UDK: |
678.074:678-1 |
COBISS: |
4487452
|
ISSN: |
1318-0207 |
Št. ogledov: |
1587 |
Št. prenosov: |
61 |
Ocena: |
0 (0 glasov) |
Metapodatki: |
|
Ostali podatki
Sekundarni jezik: |
Slovenski jezik |
Sekundarni povzetek: |
Recent investigations have shown that modification of polymer matrix with filler and elastomers significantly affects composite's mechanical properties. Isotactic PP modified with either untreated or treated talc and either SEBS or SEBS-gMA were used in these investigations. Samples were prepared by melt-mixing in a Brabender kneading chamber and were compression molded into plates on a laboratory press. The composites were characterised by measuring mechanical properties (Young's modulus, yield stress, notched impact strength) and by defining morphology. Binary sistems PP/talc and PP/elastomer containing up to 16 vol.% of talc and up to 10 vol.% of elastomer, as well as ternary PP/talc/elastomer composites with 12 vol.% talc were investigated. Ternary composite's yield stress was also calculated by semiempirical equations. We have found out, that the use of treated modifiers (talc or elastomer) improves adhesion with matrix, which reflects on mechanical properties as better stress transfer. |
Sekundarne ključne besede: |
organska kemija;polimeri;termoplasti;kompoziti;karakterizacija;kemija;plastične mase;elastomeri;morfologija;mehanske lastnosti; |
URN: |
URN:NBN:SI |
Vrsta dela (COBISS): |
Znanstveno delo |
Strani: |
str. 55-67 |
Letnik: |
46 |
Zvezek: |
ǂšt. ǂ1 |
Čas izdaje: |
1999 |
ID: |
1749812 |