Preučevali smo modifikacijo polipropilena (PP) z wollastonitom kot polnilom. V ta namen smo uporabili tri različne tipe wollastonitov, obdelanih z različnimi silani. Vzorce kompozitov smo pripravili v talini v Brabenderjevem gnetilniku in s stiskanjem v plošče v laboratorijski stiskalnici. Predvideli smo jakost adhezije med uporabljenimi polnili in PP matriko na osnovi izračunanih adhezijskih parametrov (adhezijsko delo, prosta energija medpovršine in koeficient omočenja), ki smo jih izračunali iz prostih energij površine posameznih komponent. Za določanje proste energije površine komponent smo uporabili metodo kontaktnega kota. Dobljene vrednosti adhezijskih parametrov na medpovršini smo korelirali z mehanskimi lastnosti in morfološkimi raziskavami preučevanih kompozitov in pri tem ugotovili njihovo dobro skladnost z rezultati mehanskih lastnosti. Močnejša adhezija v preučevanih PP/wollastonit kompozitih se je odražala v višjih vrednostih meje plastičnosti in pretržne trdnosti, medtem ko so bile vrednosti raztezka ob pretrgu in zarezne udarne žilavosti nižje.

Ključne besede

polipropilen;morfologija;mehanske lastnosti;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UM EPF - Ekonomsko-poslovna fakulteta
Založnik: Slovensko kemijsko društvo
UDK: 678.742
COBISS: 8262428 Povezava se bo odprla v novem oknu
ISSN: 1318-0207
Št. ogledov: 1212
Št. prenosov: 91
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarni povzetek: Modification of polypropylene (PP) with wollastonite fillers was investigated in this paper. Three types of different silane pretreated wollastonite mineral filler were used for preparation of binary PP/wollastonite composites. The composite samples were homogenized in a Brabender Plasti-Corder kneading chamber and compression moulded into plates on a laboratory press. The adhesion between the wollastonite fillers used in this study and the PP matrix was predicted on the basis of the calculated adhesion parameters (work of adhesion, interfacial free energy and spreading coefficient) obtained by the surface free energy of pure materials. The contact angle method was used to determine surface free energy of components. The obtained values of adhesion parameters at the interface in the composites were correlated with mechanical properties as well as morphology observations of corresponding composites and were proved to be in relatively good agreement with the mechanical property measurements. Stronger adhesion in investigated composites has reflected in higher yield stress and tensile strength at break but in lower elongation at break and impact resistance.
Sekundarne ključne besede: polipropilenski kompoziti;wollastonit;površinska energija;adhezija;morfologija;mehanske lastnosti;
URN: URN:NBN:SI
Vrsta dela (COBISS): Znanstveno delo
Strani: str. 264-271
Letnik: ǂVol. ǂ52
Zvezek: ǂno. ǂ3
Čas izdaje: 2005
ID: 1742909