diplomsko delo univerzitetnega študijskega programa I. stopnje
Maja Ivanovski (Avtor), Andreja Goršek (Mentor), Samo Lubej (Komentor)

Povzetek

Teoretični del diplomske naloge prikazuje analizo komponent betona, proizvedenega z uporabo recikliranih materialov. V praktičnem delu smo prikazali izdelavo vzorcev betona, ki smo jim z dodanim elektrofiltrskim pepelom (EFP) želeli zmanjšati količino cementa. V betonsko mešanico smo vmešali dve vrsti EFP. Prva serija vzorcev je bila izdelana z EFP, ki je bil proizveden iz rjavega premoga, drugi del vzorcev pa z EFP iz lignita. Z kemijsko analizo smo ugotovili, da je v EFP iz rjavega premoga več reaktivne komponente SiO2, v EFP iz lignita pa je več reaktivne komponente CaO. Prav tako smo del mineralnega agregata nadomestili z gumenimi sekanci. Preiskave vzorcev otrdelega betona po končanem vezanju so potrdile hipotezo, da je beton z dodanimi sekanci iz gume elastičen material. Meritve so pokazale, da ima beton z dodatkom gumenih sekancev in EFP iz rjavega premoga višji modul elastičnosti kot beton, ki smo mu dodali EFP iz lignita.

Ključne besede

elektrofiltrski pepel;gumeni sekanci;beton;modul elastičnosti;diplomske naloge;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UM FKKT - Fakulteta za kemijo in kemijsko tehnologijo
Založnik: [M. Ivanovski]
UDK: 691.334:665.94(043.2)
COBISS: 20364054 Povezava se bo odprla v novem oknu
Št. ogledov: 1020
Št. prenosov: 102
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: ELASTIC PROPERTIES CONTROL OF CONCRETE WITH RUBBER CHIPS ADDITION
Sekundarni povzetek: The theoretical part of the thesis presents an analysis of the components of concrete, manufactured using recycled materials. In the practical part we have shown the production of samples of concrete with the addition of fly ash (EFP), which was added in order to reduce the amount of cement. The concrete mixture was interfered by two types EFP. The first set of samples was made with EFP which is produced from brown coal, the second part of the samples with EFP lignite. The chemical analysis showed that the EFP from brown coal has more reactive components of SiO2, meanwhile the EFP from lignite has more reactive components of CaO. The part of mineral agreggate was also replaced with rubber chips. Examination of samples hardened concrete after tying confirmed the hypothesis that the concrete with added rubber chips is elastic material. Measurements have shown that the concrete with the addition of rubber chips and EFP from brown coal havr higher modulus of elasticity than concrete added with EFP lignite.
Sekundarne ključne besede: flay ash;rubber chips;concrete;modulus of elasticity;
URN: URN:SI:UM:
Vrsta dela (COBISS): Diplomsko delo/naloga
Komentar na gradivo: Univ. v Mariboru, Fak. za kemijo in kemijsko tehnologijo
Strani: VIII, 37 str.
ID: 9166284
Priporočena dela:
, diplomsko delo univerzitetnega študijskega programa I. stopnje
, diplomsko delo visokošolskega študijskega programa
, diplomsko delo visokošolskega študijskega programa
, diplomska naloga št.: 209/OG-MK