diplomska naloga št.: 209/OG-MK
Jaka Krnc (Avtor), Violeta Bokan-Bosiljkov (Mentor)

Povzetek

V diplomski nalogi so obravnavane lastnosti betonskih mešanic, katerih vezivo predstavlja žlindrin cement CEM III/B 32,5 N-LH/SR, z nizko toploto hidratacije. Za pridobitev podatkov o lastnostih različnih mešanic so bile opravljene laboratorijske preiskave svežega in strjenega betona. Na svežih mešanicah so bile opravljene preiskave za določitev konsistence (metoda s posedom in metoda z razlezom), na strjenih vzorcih pa so bili določeni tlačna trdnost s porušno metodo in elastični parametri z uporabo ultrazvočne preiskave. Enake preiskave so bile opravljene tudi na betonih s Portlandskim cementom CEM II/B-M (LL-V) 42,5 N. Cementi CEM II/B so najpogosteje uporabljena vrsta cementa v slovenski gradbeniški praksi. Sledila je analiza rezultatov in njihova medsebojna primerjava. Rezultati so pokazali, da so betoni z žlindrinim cementom bolj tekoče konsistence, kot betoni s Portlandskim cementom. Zgodnje vrednosti mehanskih lastnosti, kot so tlačna trdnost ter dinamični modul elastičnosti in strižni modul, so občutno nižje pri betonih z žlindrinim cementom, zaradi počasnejšega oblikovanja produktov hidratacije. Po osemindvajsetih dneh hidratacije pa se razlika tlačnih trdnosti in elastičnih parametrov med betoni z žlindrinim cementom in betoni s Portlandskim cementom bistveno zmanjša. V nekaterih primerih betoni z žlindrinim cementom dosežejo celo višje 28-dnevne vrednosti mehanskih lastnosti.

Ključne besede

gradbeništvo;diplomska naloga;VSŠ;GR;GR-OG;beton;žlindrin cement;preskus s posedom;preskus z razlezom;tlačna trdnost;ultrazvok;modul elastičnosti;strižni modul;Poissonov koeficient;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FGG - Fakulteta za gradbeništvo in geodezijo
Založnik: [J. Krnc]
UDK: 691.32(497.4)(043.2)
COBISS: 84670211 Povezava se bo odprla v novem oknu
Št. ogledov: 286
Št. prenosov: 58
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Properties of slag cement concrete
Sekundarni povzetek: he graduation thesis deals with the properties of concrete mixtures prepared with slag cement CEM III / B 32.5 N-LH / SR with low heat of hydration. Laboratory tests of fresh and hardened concrete were performed to obtain data on the properties of different mixtures. Slump test and flow table test were performed to determine the consistency of fresh concrete. Compressive strength was determined on hardened samples and elastic parameters were measured using the ultrasonic technique. The same tests were performed on concretes with Portland cement CEM II / B-M (LL-V) 42.5 N. CEM II / B types of cement are the most commonly used cements in Slovenian construction practice. After completed laboratory tests, an analysis of the test results and their comparison followed. The obtained results showed that slag cement concretes have a more liquid consistency than Portland cement concretes. Due to the slower formation of hydration products, early age mechanical properties, such as compressive strength and dynamic modulus of elasticity and shear modulus, are significantly lower in the slag cement concretes. After twenty-eight days of binder hydration, the difference in compressive strength and elastic parameters between the slag cement concrete and Portland cement concrete decreases significantly. In some cases, slag cement concrete achieves even higher mechanical properties after twenty eight days.
Sekundarne ključne besede: graduation thesis;civil engineering;concrete;slag cement;slump test;flow table test;compressive strength;ultrasound;modulus of elasticity;shear modulus;Poisson's ratio;
Vrsta dela (COBISS): Diplomsko delo/naloga
Komentar na gradivo: Univ. v Ljubljani, Fak. za gradbeništvo in geodezijo
Strani: XVI, 44 str.