Franc Zupanič (Avtor), Tonica Bončina (Avtor), Niko Rozman (Avtor), Ivan Anžel (Avtor), Werner Grogger (Avtor), Christian Gspan (Avtor), Ferdinand Hofer (Avtor), Boštjan Markoli (Avtor)

Povzetek

An Al94Mn2Be2Cu2 cast alloy was developed displaying increased quasicrystalline formation ability at moderate cooling rates. The as-cast microstructure consisted of a mainly icosahedral phase in the Al-matrix. The microstructure remained stable during uniform heating to 580 °C and isothermalannealing at 400 °C. Most of the icosahedral phase was preserved even after 24 h annealing at 500 °C. For that reason, this alloy presents a promising basis for further development of cast Al-alloys containing quasicrystals.

Ključne besede

Al-Mn-Be-Cu zlitine;kvazikristali;kvazikristalinične faze;alluminium alloys;casting;quasicrystals;TEM;SEM;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.08 - Objavljeni znanstveni prispevek na konferenci
Organizacija: UM FS - Fakulteta za strojništvo
UDK: 669.71:539
COBISS: 13027094 Povezava se bo odprla v novem oknu
ISSN: 0044-2968
Št. ogledov: 1574
Št. prenosov: 94
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarne ključne besede: Al-Mn-Be-Cu zlitine;kvazikristali;kvazikristalinične faze;
URN: URN:SI:UM:
Strani: Str. 735-738
Ključne besede (UDK): applied sciences;medicine;technology;uporabne znanosti;medicina;tehnika;chemical technology;chemical and related industries;kemijska tehnologija;kemijske in sorodne industrije;metallurgy;metalurgija;mathematics;natural sciences;naravoslovne vede;matematika;physics;fizika;physical nature of matter;fizikalna zgradba snovi;
DOI: 10.1524/zkri.2008.1037
ID: 1005741