Marko Dunđer (Avtor), Tomaž Vuherer (Avtor), Ivan Samardžić (Avtor)

Povzetek

The paper presents research of weldability of microalloyed high strength steels TStE 420 and S960QL after weld thermal cycle simulation. Beside mechanical properties hardness and impact strength, the microstructures of characteristic weld thermal cycled structures for both steels are given. The results will contribure to determination of weakest points in Heat Affected Zone of both steels.

Ključne besede

varjenje;visokotrdnostna jekla;mehanske lastnosti;TStE 420;S960QL;weldabilty;high strength steels;mechanical properties;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UM FS - Fakulteta za strojništvo
UDK: 621.9.02
COBISS: 17756182 Povezava se bo odprla v novem oknu
ISSN: 0543-5846
Št. ogledov: 1823
Št. prenosov: 110
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarne ključne besede: varjenje;visokotrdnostna jekla;mehanske lastnosti;TStE 420;S960QL;
URN: URN:SI:UM:
Vrsta dela (COBISS): Znanstveno delo
Strani: str. 335-338
Letnik: ǂVol. ǂ53
Zvezek: ǂiss. ǂ3
Čas izdaje: 2014
ID: 10846234